Dissertations / Theses on the topic 'Sistemi adesivi'

Polymeric adhesives have been used for many applications like suture and embolization, instead of classic surgical methods or as for dental uses. In this work both subjects have been investigated and the results separated in two parts. In the first, new dentinal adhesives with different polymerizable groups (methacrylic or vinyl-ethereal) were synthesized. A low sensitivity to hydrolysis and equal or enhanced properties, compared to existing commercial products, were considered essentials. Moreover, these monomers need to polymerize by radical photopolymerization and functional groups of different characteristics were tested. All these products were characterized by microtensile bond strength test to determine the bonding strength between the adhesive and tooth. Concerning embolization, cyanoacrylates are nowadays the most-used adhesives in surgery. Thus, they must respond to several requirements. For instance, polymerization time and adhesive strength need to be low, to avoid diffusion of the products in the body and adhesion to the catheter. In order to overcome these problems we developed new cyanoacrylates, which practically instantly polymerize upon contact with blood but do not demonstrate strong adhesion to the catheter, thank to the presence of fluorine atoms, linked to the ester chain. The synthesis of these products was carried out in several steps, such as the depolymerization of the corresponding oligomers at high temperature in acid conditions. Two types of adhesion strengths were determined. Bonding strength between human veins and a microcatheter was determined in vitro by using organic materials as the most realistic model. Another test, on two layers of skin, was conducted to verify the possible use of these new cyanoacrylates as a glue for sutures. As a conclusion, we were able to demonstrate that some of the prepared monomers posses adhesive strength and polymerization time lower than the commercial product Glubran2.

Polymeric adhesives have been used for many applications like suture and embolization, instead of classic surgical methods or as for dental uses. In this work both subjects have been investigated and the results separated in two parts. In the first, new dentinal adhesives with different polymerizable groups (methacrylic or vinyl-ethereal) were synthesized. A low sensitivity to hydrolysis and equal or enhanced properties, compared to existing commercial products, were considered essentials. Moreover, these monomers need to polymerize by radical photopolymerization and functional groups of different characteristics were tested. All these products were characterized by microtensile bond strength test to determine the bonding strength between the adhesive and tooth. Concerning embolization, cyanoacrylates are nowadays the most-used adhesives in surgery. Thus, they must respond to several requirements. For instance, polymerization time and adhesive strength need to be low, to avoid diffusion of the products in the body and adhesion to the catheter. In order to overcome these problems we developed new cyanoacrylates, which practically instantly polymerize upon contact with blood but do not demonstrate strong adhesion to the catheter, thank to the presence of fluorine atoms, linked to the ester chain. The synthesis of these products was carried out in several steps, such as the depolymerization of the corresponding oligomers at high temperature in acid conditions. Two types of adhesion strengths were determined. Bonding strength between human veins and a microcatheter was determined in vitro by using organic materials as the most realistic model. Another test, on two layers of skin, was conducted to verify the possible use of these new cyanoacrylates as a glue for sutures. As a conclusion, we were able to demonstrate that some of the prepared monomers posses adhesive strength and polymerization time lower than the commercial product Glubran2.

This study was dealt with the development of polymeric adhesive systems to be used in innovative junction processes based on friction stir welding (FSW) technology, and in particular on the hybrid technique FSW-bonding, for joining elements composed of metal alloys. The addition of suitable additives, such as inorganic fillers, to the most promising formulations was aimed at obtaining materials not only leading to a stronger adhesion between the phases, but also characterized by improved thermal properties and good resistance to oxidation and chemical attacks. Furthermore, due to their relevance in the naval industries, studies on structural adhesive containing expandable reactive agents designed to lose adhesiveness due to heating due was performed. These materials incorporated into adhesive systems promote the disassembly and/or repair of bonded structures favoring recycle for ensure a high environmentally friendly. An innovative strategy for structural adhesive joint debonding by using an infrared heating system and the utilization of thermally expandable microparticles (TEMs) was studied.

Made available in DSpace on 2014-06-11T19:24:07Z (GMT). No. of bitstreams: 0 Previous issue date: 2007-07-26Bitstream added on 2014-06-13T20:51:29Z : No. of bitstreams: 1 marimoto_ark_me_sjc.pdf: 390443 bytes, checksum: d76f9139d735bc954e3a1f9a3c6ec8ce (MD5)
Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
A adesão continua a ser um desafio na Odontologia, principalmente em tecidos morfologicamente distintos e valendo-se de sistemas adesivos de mecanismos de ação também distintos. O objetivo deste estudo in vitro foi comparar a resistência adesiva de dois sistemas (autocondicionante e convencional) em dois substratos (esmalte e dentina), associados ou não à tecnologia laser (Nd:YAG). Foram utilizados 120 dentes bovinos, recém-extraídos, embutidos, que tiveram a superfície de esmalte ou dentina exposta por meio de lixas. Uma área de 3mm de diâmetro na região cérvico-vestibular-mediana foi selecionada para adesão, de acordo com os seguintes grupos: a) G1: AF/ esmalte (adesivo autocondicionante em esmalte seguindo especificação do fabricante); b) G2: AF/ dentina (adesivo autocondicionante em dentina seguindo especificação do fabricante); c) G3: AL/ esmalte (adesivo autocondicionante em esmalte + laser Nd:YAG + fotopolimerização); d) G4: AL/ dentina (adesivo autocondicionante em dentina + laser Nd:YAG + fotopolimerização); e) G5: CF/ esmalte (condicionamento ácido + adesivo convencional em esmalte); f) G6: CF/ dentina (condicionamento ácido + adesivo convencional em dentina); g) G7: CL/ esmalte (condicionamento ácido + adesivo convencional em esmalte + laser Nd:YAG + fotopolimerização); h) G8: CL/ dentina (condicionamento ácido + adesivo convencional em dentina + laser Nd:YAG + fotopolimerização). A resina composta Z 250 foi inserida com auxílio de matriz de teflon e fotopolimerizada com luz halógena, seguida da realização do teste de cisalhamento em máquina universal Emic, com carga de100kgf e velocidade de 0,5mm/min. Os valores médios em MPa obtidos para os diferentes grupos foram: G1 (20,291), G2 (14,142), G3 (23,615), G4 (22,235), G5 (20,899), G6 (11,291), G7 (22,102), G8 (15,980). Após aplicação do teste de ANOVA e Tukey 5%, concluiu-se que...
Bonding continues to be a challenge in Dentistry, particularly in morphologically different tissues, and adhesive systems with different action mechanisms are also valid. The aim of this study was to compare the bond strength of two systems (self-etching and conventional) to two substrates (enamel and dentin) either associated with laser technology (Nd:YAG) or not. One hundred and twenty (120) recently extracted, embedded bovine teeth were used, and abrasive papers were used to expose the enamel or dentin surfaces. An area of 3mm in diameter in the cervical-vestibular-median region was selected for bonding, according to the following groups: a) G1: AF/ enamel (self-etching adhesive to enamel in accordance with the manufacturer's specification); b) G2: AF/ dentin (self-etching adhesive to dentin in accordance with the manufacturer's specification); c) G3: AF/ enamel (self-etching adhesive to enamel + laser Nd:YAG + light polymerization ; d) G4: AL/ dentin (self-etching adhesive to dentin + laser Nd:YAG + light polymerization ; e) G5: CF/ enamel (acid etching + conventional adhesive to enamel); f) G6: CF/ dentin (acid etching + conventional adhesive to dentin); g) G7: CL/ enamel (acid etching + conventional adhesive to enamel + laser Nd:YAG + light polymerization ; h) G8: CL/ dentin (acid etching + conventional adhesive to dentin + laser Nd:YAG + light polymerization). Resin composite Z250 was inserted with the aid of a Teflon matrix and light polymerized, followed by the shear test in an EMIC universal machine, with a load of 100 Kgf and speed of 0.5 mm/min. The mean values obtained in Mpa for the different groups were: G1 (20.291), G2 (14.142), G3 (23.615), G4 (22.235), G5 (20.899), G6 (11.291), G7 (22.102), G8 (15.980). After applying the ANOVA and Tukey tests 5%, it was concluded that the application of laser Nd:YAG significantly increased the bond strength under all the experimental... (Complete abstract click electronic access below)

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior
This study aimed to evaluate the effects of dentin pretreatment and temperature on the bond strength of a universal adhesive system to dentin. Ninety-six extracted non-carious human third molars were randomly divided into 12 groups (n=8) according to Scotchbond Universal Adhesive (SbU) applied in self-etch (SE) and total-etch (TE) mode, adhesive temperature (20ºC or 37ºC) and sodium bicarbonate or aluminum oxide air abrasion. After composite build up, bonded sticks with cross-sectional area of 1 mm² were obtained to evaluate the microtensile bond strength (μTBS). The specimens were tested at a crosshead speed of 0.5 mm/min on a universal testing machine until failure. Fractured specimens were analyzed under stereomicroscope to determine the failure patterns in adhesive, cohesive (dentin or resin) and mixed fractures. The microtensile bond strength data was analyzed using to two-way ANOVA and Tukey s test (p<0.01). Interaction between treatment and temperature was statistically significant to SbU applied in SE technique. Both dentin treatments showed higher bond strength to TE mode, regardless of adhesive temperature. When compared to control group, sodium bicarbonate increased bond strength of SbU in SE mode. Adhesive temperature did not significantly affect the μTBS of tested groups. Predominantly, adhesive failure was observed for all groups. Thus, the dentin pretreatment may be an alternative to improve the adhesive properties of the Scotchbond Universal adhesive system.
O presente estudo avaliou os efeitos do jateamento de partículas abrasivas e da temperatura sobre a resistência adesiva de um sistema adesivo universal à dentina. Utilizou-se 96 terceiros molares humanos hígidos e extraídos, divididos aleatoriamente em 12 grupos (n=8) de acordo com o adesivo Scotchbond Universal (SBU) aplicado no modo autocondicionante (SE) ou condicionamento ácido total (TE), temperatura do adesivo (20ºC ou 37ºC) e jateamento da dentina com partículas de óxido de alumínio ou bicarbonato de sódio. Após a realização das restaurações, foram obtidos espécimes em forma de palito com área seccional de 1 mm² para avaliar a resistência adesiva através do teste de microtração. O teste foi realizado em uma máquina de ensaio universal, a uma velocidade de 0,5 mm/min até a fratura ocorrer. As fraturas foram analisadas sob estereomicroscopia para classificar as falhas em adesiva, coesiva (resina ou dentina) e mista. Os dados foram submetidos ao teste ANOVA a dois fatores e ao teste de Tukey. A interação entre tratamento e temperatura foi estatisticamente significante (p<0,01) para SBU SE. Ambos os tratamentos da dentina resultaram em valores maiores de resistência adesiva para SBU no modo TE, independente da temperatura do adesivo. Já para SBU aplicado na técnica autocondicionante, apenas o jateamento com bicarbonato de sódio foi significativamente diferente quando comparado ao grupo que não recebeu tratamento. O adesivo aquecido não teve influência significativa sobre a resistência adesiva à microtração, para todos os grupos testados. As fraturas adesivas foram predominantes para todos os grupos. Dessa forma, o pré-tratamento dentinário pode ser uma alternativa para melhorar as propriedades adesivas do sistema adesivo Scotchbond Universal.

Made available in DSpace on 2014-06-11T19:35:03Z (GMT). No. of bitstreams: 0 Previous issue date: 2008-10-30Bitstream added on 2014-06-13T18:46:01Z : No. of bitstreams: 1 martinjunior_m_dr_araca.pdf: 402142 bytes, checksum: ec08401476b3983abaa71ed519f0d4e8 (MD5)
OBJETIVO: Avaliar a distribuição das tensões na interface dentina-adesivo variando o sistema adesivo, convencional e autocondicionante, através do método dos elementos finitos tridimensional. MATERIAL E MÉTODO: Foram elaborados 4 modelos no programa Solidworks 2007, sendo: Mc - representação de um espécime em dentina (41x41x82 μm) restaurado com resina composta (RC), apresentando camada de adesivo, camada híbrida (CH), TAGs, dentina peri-tubular, dentina intertubular parcialmente desmineralizada, dentina intertubular e prolongamento odontoblástico, simulando a formação da CH segundo o sistema adesivo convencional; Mr - idêntico ao Mc, com ramificações laterais do infiltrado do adesivo; Ma – idêntico ao Mc, sem TAGs, e com “smear plug”, simulando o sistema adesivo autocondicionante; Mat – idêntico ao Ma, com TAGs. Os modelos foram considerados isotrópicos, homogêneos e linearmente elásticos e a análise numérica foi realizada no ANSYS Workbench 10.0 para obtenção da máxima tensão principal (MAX) após aplicação de força de tração de 0,03 N perpendicular à superfície da RC. A base de todos os modelos foi fixada nos eixos x, y e z. RESULTADOS: A MAX foi maior para o sistema convencional. A presença da ramificação lateral aumentou a MAX na CH para o sistema convencional. Os TAGs modificaram a distribuição da MAX na camada de adesivo para o sistema autocondicionante. CONCLUSÃO: A CH para o sistema convencional apresentou maior MAX em comparação ao sistema autocondicionante. A presença das ramificações laterais do adesivo aumentaram a tensão na CH para o sistema convencional.
OBJECTIVE: The aim of this study was to evaluate the stress distribution in the hybrid layer varying the adhesive system (total each and self-etching systems) using three-dimensional finite element analysis (FE). METHODS: 4 FE models (M) were developed in Solidworks 2007: Mc - representation of a specimen of dentin (41x41x82 μm) restored with composite resin (RC), showing the adhesive layer, hybrid layer (HL), TAGs, peri-tubular dentin, intertubular dentin in order to simulate simulating the HL according to the total-etch adhesive system; Mr - similar to Mc, with lateral branches of the adhesive; Ma – similar to Mc, without TAGs and showing the smear plug in order to simulate the environment for the self-ethcing adhesive system; Mat – similar to Ma, with TAGs. The models were considered isotropic, homogeneous and linearly elastic and numerical analysis was performed in ANSYS Workbench 10.0 to obtain the maximum principal stress (MAX) after application of a tension force of 0.03N perpendicular to the surface of the RC. The botton of all models was fixed in x, y and z axis. RESULTS: The highest MAX in HL was observed in the total etching system. The lateral branches increased the MAX in HL. The TAGs had a little influence on the stress distribution in self-ethching system. CONCLUSION: The HL for the total-etch system showed MAX higher in comparison with the self-etch system. The presence of TAGs increased the MAX in the HL for the total-etch system.

Orientador: Eduardo Passos Rocha
Banca: Marco Antonio Luersen
Banca: Renato Herman Sundfeld
Banca: Marcelo Giannini
Banca: Washington Rodrigues Camargo
Resumo: OBJETIVO: Avaliar a distribuição das tensões na interface dentina-adesivo variando o sistema adesivo, convencional e autocondicionante, através do método dos elementos finitos tridimensional. MATERIAL E MÉTODO: Foram elaborados 4 modelos no programa Solidworks 2007, sendo: Mc - representação de um espécime em dentina (41x41x82 μm) restaurado com resina composta (RC), apresentando camada de adesivo, camada híbrida (CH), TAGs, dentina peri-tubular, dentina intertubular parcialmente desmineralizada, dentina intertubular e prolongamento odontoblástico, simulando a formação da CH segundo o sistema adesivo convencional; Mr - idêntico ao Mc, com ramificações laterais do infiltrado do adesivo; Ma - idêntico ao Mc, sem TAGs, e com "smear plug", simulando o sistema adesivo autocondicionante; Mat - idêntico ao Ma, com TAGs. Os modelos foram considerados isotrópicos, homogêneos e linearmente elásticos e a análise numérica foi realizada no ANSYS Workbench 10.0 para obtenção da máxima tensão principal (MAX) após aplicação de força de tração de 0,03 N perpendicular à superfície da RC. A base de todos os modelos foi fixada nos eixos x, y e z. RESULTADOS: A MAX foi maior para o sistema convencional. A presença da ramificação lateral aumentou a MAX na CH para o sistema convencional. Os TAGs modificaram a distribuição da MAX na camada de adesivo para o sistema autocondicionante. CONCLUSÃO: A CH para o sistema convencional apresentou maior MAX em comparação ao sistema autocondicionante. A presença das ramificações laterais do adesivo aumentaram a tensão na CH para o sistema convencional.
Abstract: OBJECTIVE: The aim of this study was to evaluate the stress distribution in the hybrid layer varying the adhesive system (total each and self-etching systems) using three-dimensional finite element analysis (FE). METHODS: 4 FE models (M) were developed in Solidworks 2007: Mc - representation of a specimen of dentin (41x41x82 μm) restored with composite resin (RC), showing the adhesive layer, hybrid layer (HL), TAGs, peri-tubular dentin, intertubular dentin in order to simulate simulating the HL according to the total-etch adhesive system; Mr - similar to Mc, with lateral branches of the adhesive; Ma - similar to Mc, without TAGs and showing the "smear plug" in order to simulate the environment for the self-ethcing adhesive system; Mat - similar to Ma, with TAGs. The models were considered isotropic, homogeneous and linearly elastic and numerical analysis was performed in ANSYS Workbench 10.0 to obtain the maximum principal stress (MAX) after application of a tension force of 0.03N perpendicular to the surface of the RC. The botton of all models was fixed in x, y and z axis. RESULTS: The highest MAX in HL was observed in the total etching system. The lateral branches increased the MAX in HL. The TAGs had a little influence on the stress distribution in self-ethching system. CONCLUSION: The HL for the total-etch system showed MAX higher in comparison with the self-etch system. The presence of TAGs increased the MAX in the HL for the total-etch system.
Doutor

2013/2014
Lo scopo di questa tesi di dottorato è stato studiare l'effetto sulla durabilità dell’interfaccia adesiva del chitosano, modificato con gruppi metacrilici, con l’obiettivo di migliorare l'affidabilità clinica dei restauri dentali. Attualmente, la ricerca in questo settore mira ad aumentare la durata nel tempo del legame resina-dentina. Questa ricerca propone un nuovo concetto di sistema adesivo bi-funzionale basato su un biopolimero naturale in grado di creare doppia reticolazione covalente. Il chitosano è un polimero biocompatibile e non tossico. In questo studio è stato ipotizzato che il chitosano modificato con gruppi metacrilici sia in grado di legarsi covalentemente alla resina dei restauri dentale e, grazie alla presenza di cariche positive residue sul polisaccaride, di interagire elettrostaticamente con la dentina demineralizzata. Il Chitosano metacrilato è stato introdotto nel primer di un sistema adesivo sperimentale etch&rinse a tre passaggi per valutarne la forza di legame alla dentina. Le prove d’invecchiamento sono state condotte utilizzando due metodiche: invecchiamento statico e dinamico. Il secondo metodo simula la presenza del sistema adesivo nell’ambiente orale, sottoposto sia a carico masticatorio, che a stress termici. Le metodiche d’invecchiamento sono necessarie per valutare la stabilità nel tempo dei restauri dentali. L'introduzione del chitosano modificato con gruppi metacrilici nel primer di un sistema adesivo etch&rinse ha determinato: buoni valori di adesione dopo 24 ore (T0 μTBS); (2) buona stabilità dello strato ibrido quando sottoposto a simulazione meccanica della masticazione e stress termici (TCS μTBS). In sintesi, la prima parte di questa tesi di dottorato ha avuto lo scopo di esaminare lo stato dell'arte dei materiali dentali attualmente utilizzati in odontoiatria e il problema più importante in odontoiatria restaurativa: la degradazione dell'interfaccia adesiva. La seconda fase di questa ricerca è stata dedicata al trovare la formulazione ottimale di un sistema adesivo contenente chitosano modificato con gruppi metacrilici. Diverse formulazioni sono state testate e il sistema sperimentale identificato come A3* è stato considerato la migliore formulazione utilizzabile come sistema adesivo. Questa formulazione è stata poi nominata Chit-MA70. Sono stati eseguiti diversi test per valutare le caratteristiche dell’adesivo sperimentale, compresi test meccanici (test di microtensile). L'espressione del nanoleakage è stata valutata utilizzando la microscopia ottica e la microscopia elettronica a scansione (SEM). Per valutare la sostantività del chitosano sullo strato adesivo, il polimero è stato marcato con fluoresceina e i campioni sono stati osservati al microscopio confocale a scansione laser (CLSM). Nella fase finale di questo studio sono stati condotti test di citotossicità per valutare l'effetto del sistema adesivo Chit-MA70 sulla vitalità cellulare. Le prove eseguite su fibroblasti gengivali hanno rivelato una tossicità ridotta, se non praticamente assente, del sistema adesivo contenente chitosano metacrilato. Considerando i buoni risultati di questo studio, il chitosano modificato con gruppi metacrilici è stato proposto come componente di un sistema adesivo sperimentale. I risultati ottenuti utilizzando questo nuovo sistema adesivo sono stati rivendicati in un brevetto (febbraio 2014) e pubblicati in Biomacromolecules nel mese di ottobre (2014).
The purpose of this thesis was to investigate the effect of a methacrylate-modified chitosan on the durability of adhesive interfaces to improve the clinical performance of dental restorations. Current research in this field aims at increasing the resin-dentin bond durability. The aim of this project was the development of an innovative nano-engineered biocompatible dental adhesive system capable to form covalent chemical bonds with both the dentin collagen and the resin-based restorative materials. This research proposes a new concept of bi-functional reactive adhesive system based on a natural biopolymer capable to create double covalent reticulation. Chitosan is a biocompatible, biodegradable and non-toxic biopolymer. In the present work, chitosan was modified with methacrylate moieties and a physical-chemical characterization was carried out. This research speculated that the modified chitosan was able to covalently bind to the restorative resin and, due to the presence of residual positive charges on the polysaccharide, to electrostatically interact with the demineralized dentine. Chitosan bearing methacrylate groups was blended within the primer of a three- step etch&rinse experimental dentine bonding system to assay its bonding ability to dentine. Additionally, bonded interfaces were challenged with a chewing simulation associated with thermo cycling to assay their stability over time. The introduction of chitosan-modified monomers within the primer of an experimental three-step etch-and-rinse adhesive, improved (1) immediate bond strength (T0 μTBS); (2) stability of the hybrid layer after simulated chewing and thermo cycling (TCS μTBS). In summary, the first part of this PhD thesis aimed to review the state of the art of dental materials currently used in dentistry and the most important problem in restorative dentistry: the degradation of bonded interface focusing on the fundamental processes that are responsible for the degradation of the adhesive interface. The second part of this doctoral thesis was dedicated to find the optimal formulation of a chitosan–containing dental adhesive system. Several formulations were were tested and the one identified as A3* was considered the best formulation to be used as an adhesive system. This formulation was then named Chit-MA70. Several tests were carried out, including mechanical tests such as the microtensile bond strength test. The nanoleakage expression was evaluated using optical microscopy and scanning electron microscopy. The evaluation of the substantivity of chitosan on the adhesive layer was evaluated by labeling the methacrylate-modified chitosan, contained into the primer, with fluorescein and then observing the samples by confocal laser scanning microscopy. In the end, cytotoxicity tests were performed to evaluate the effect on cell viability of the adhesive system Chit-MA70. Tests carried out on gingival fibroblasts revealed a reduced if not practically absent toxicity of the adhesive system containing methacrylate-modified chitosan. Considering the good results of this study, the methacrylate-modified chitosan has been proposed as a component of a novel adhesive system. The findings on this new dental adhesive with methacrylate-modified chitosan were claimed into a patent in February 2014 and published in Biomacromolecules in October 2014.
XXVII Ciclo
1986

Made available in DSpace on 2015-01-26T13:21:26Z (GMT). No. of bitstreams: 0 Previous issue date: 2005-06-13Bitstream added on 2015-01-26T13:30:28Z : No. of bitstreams: 1 000326687.pdf: 2821504 bytes, checksum: 1d66d1ded90d9d6ea873a9687a44bde1 (MD5)
Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
Este estudo foi realizado no intuito de avaliar a resistência de união à dentina coronária e do canal radicular com dois sistemas adesivos de condicionamento total (dois e três passos) e um sistema autocondicionante. Os canais de trinta incisivos e caninos humanos superiores foram instrumentados e preparados com brocas. Os pinos usados na cimentação foram réplicas em cimento resinoso dual Duo-link do pino Aestheti Plus #2. Assim, constituíram-se três grupos (n = 10), segundo o sistema adesivo utilizado: condicionamento total três passos (CT3) - AII-Bond 2 + pino em cimento resinoso (pcr)+ Duo-link (DI); condicionamento total 2 passos (CT2) - One-Step Plus + pcr + DI; autocondicionante (AC) - Tyrian/One-Step Plus+ pcr + DI. Apôs a cimentação, foram obtidas oito secções transversais (1,5mm), a partir de 4mm acima da JEC até 4mm aquém do ápice do canal, envolvendo dentina coronária e radicular. As secções foram submetidas ao ensaio de push-out em máquina de ensaio universal EMIC (1 mm.min-1). Os dados de resistêncía adesiva foram analisados com o teste ANOVA de dois fatores de medidas repetidas (α<0,05). Foi observado que o efeito interação foi estatisticamente significante, isto é, o relacionamento entre os adesivos não foi o mesmo para as diferentes regiões. Comparando-se as médias obtidas com os adesivos em cada região (Tukey; α<0,05), observou-se que o CT3 (média± desvio padrão: 5,22 ± 1,70) foi superior ao CT2 (2,60 ± 1,74) e ao AC (1,68 ± 1,85). Para as condições estudadas, obteve-se melhor adesão à dentina com a utilização do sistema adesivo de condicionamento total com três passos, sobretudo na região coronária
This study aimed to evaluate lhe bond strengths between two total etching adhesive systems and (two and three steps) anda self-etching system to coronal and root canal dentin. The root canal of thirty human anterior teeth were endodontically instrumented and prepared with specific burs. Aestheti Plus #2 posts were duplicated in dual resin cement (Duo-link) and three groups (n=10) were formed, according to the adhesive sysfem used: 3 steps total etching adhesive system (3TE) - All-Bond 2 + resin cement post (rcp) + Duo-link (DI); 2 steps total etching adhesive system (2TE) - One-Step Plus + rcp + DI; sef-etching system (SE) Tyrian/One-Step Plus + rcp +DI. Following cementation, the teeth were cut transversally in eight sections (1,5mm), from the CEJ to 4mm above the canal apex. The sections were subjected to the push-out test in a universal testing machine (1mm.min-1). The data of bond strength were statistically analyzed with 2-way Anova of repeated measures (α<0.05), which showed that the interaction effect was significant. This meant that the relationship between the adhesives was not the same depending on the tooth region. Regarding the adhesive factor'' the comparison of means with Tukey test (α<0.05) showed that 3TE (mean ± standard deviation: 5,22 ± 1,70) was statistically superior to 2TE (2,60 ± 1,74) and SE (1,68 ± 1,85). Under the conditions of the present study, the three step total etching system had the highest bond strengths to dentin, especially in the coronal region

Orientador: Carlos Augusto Pavanelli
Banca: Paulo Sérgio Mutarelli
Banca: Carlos Rocha Gomes Torres
Resumo: Este estudo foi realizado no intuito de avaliar a resistência de união à dentina coronária e do canal radicular com dois sistemas adesivos de condicionamento total (dois e três passos) e um sistema autocondicionante. Os canais de trinta incisivos e caninos humanos superiores foram instrumentados e preparados com brocas. Os pinos usados na cimentação foram réplicas em cimento resinoso dual Duo-link do pino Aestheti Plus #2. Assim, constituíram-se três grupos (n = 10), segundo o sistema adesivo utilizado: condicionamento total três passos (CT3) - AII-Bond 2 + pino em cimento resinoso (pcr)+ Duo-link (DI); condicionamento total 2 passos (CT2) - One-Step Plus + pcr + DI; autocondicionante (AC) - Tyrian/One-Step Plus+ pcr + DI. Apôs a cimentação, foram obtidas oito secções transversais (1,5mm), a partir de 4mm acima da JEC até 4mm aquém do ápice do canal, envolvendo dentina coronária e radicular. As secções foram submetidas ao ensaio de push-out em máquina de ensaio universal EMIC (1 mm.min-1). Os dados de resistêncía adesiva foram analisados com o teste ANOVA de dois fatores de medidas repetidas (α<0,05). Foi observado que o efeito interação foi estatisticamente significante, isto é, o relacionamento entre os adesivos não foi o mesmo para as diferentes regiões. Comparando-se as médias obtidas com os adesivos em cada região (Tukey; α<0,05), observou-se que o CT3 (média± desvio padrão: 5,22 ± 1,70) foi superior ao CT2 (2,60 ± 1,74) e ao AC (1,68 ± 1,85). Para as condições estudadas, obteve-se melhor adesão à dentina com a utilização do sistema adesivo de condicionamento total com três passos, sobretudo na região coronária
Abstract: This study aimed to evaluate lhe bond strengths between two total etching adhesive systems and (two and three steps) anda self-etching system to coronal and root canal dentin. The root canal of thirty human anterior teeth were endodontically instrumented and prepared with specific burs. Aestheti Plus #2 posts were duplicated in dual resin cement (Duo-link) and three groups (n=10) were formed, according to the adhesive sysfem used: 3 steps total etching adhesive system (3TE) - All-Bond 2 + resin cement post (rcp) + Duo-link (DI); 2 steps total etching adhesive system (2TE) - One-Step Plus + rcp + DI; sef-etching system (SE) Tyrian/One-Step Plus + rcp +DI. Following cementation, the teeth were cut transversally in eight sections (1,5mm), from the CEJ to 4mm above the canal apex. The sections were subjected to the push-out test in a universal testing machine (1mm.min-1). The data of bond strength were statistically analyzed with 2-way Anova of repeated measures (α<0.05), which showed that the interaction effect was significant. This meant that the relationship between the adhesives was not the same depending on the tooth region. Regarding the "adhesive factor'' the comparison of means with Tukey test (α<0.05) showed that 3TE (mean ± standard deviation: 5,22 ± 1,70) was statistically superior to 2TE (2,60 ± 1,74) and SE (1,68 ± 1,85). Under the conditions of the present study, the three step total etching system had the highest bond strengths to dentin, especially in the coronal region
Mestre

O objetivo desse trabalho foi avaliar a influência da resistência de união de sistemas adesivos à dentina irrigada com substâncias endondônticas, após a degradação da interface adesiva e análise morfológica da interface adesiva por meio de microscopia eletrônica de varredura (MEV). Foram selecionados sessenta terceiros molares, que tiveram a porção oclusal removida e planificada expondo a dentina profunda. Os espécimes foram irrigados com hipoclorito de sódio a 2,5% por 30 minutos e em seguida em EDTA 17% por 5 minutos. Após a irrigação da superfície detinária os dentes foram divididos aleatoriamente em seis grupos (n = 10) de acordo com o sistema adesivo empregado: G1 e G2 - Clearfil (Kuraray); G3 e G4 - Single Bond 2 (3M) e G5 e G6 - XP Bond (Dentsply). Após a aplicação do sistema adesivo, foi confeccionado um platô de resina composta Z100 (3M). A degradação da interface adesiva foi realizada por meio de estocagem em água deionizada/ciclagem térmica: 24 horas de estocagem em água deionizada/nenhum ciclo (grupos G1, G3 e G5) e 6 meses de estocagem em água deionizada/12.000 ciclos (grupos G2, G4 e G6). Após os períodos pré-estabelecidos em cada grupo, os conjuntos dente/resina foram seccionados de forma a se obter 4 palitos de aproximadamente de 1mm2, que foram submetidos ao teste de microtração. A análise morfológica da interface foi realizada por meio de MEV. Os dados obtidos foram submetidos a ANOVA e teste de Tukey ao nível de 5%. Verificou-se que houve diferença significativa entre os adesivos (p<0,01). A durabilidade da adesão da resina composta a dentina irrigada com solução endodôntica não foi afetada após 6 meses de estocagem em água e 12.000 ciclos térmicos (p<0,05). A análise da interface adesiva evidenciou que os sistemas adesivos não alteraram o padrão de união mesmo após 6 meses de ciclagem térmica e degradação em água, exceto para o sistema adesivo XP Bond. Pode-se concluir que a dentina irrigada com NaOCl e EDTA apresentou menor resistência a microtração quando do emprego do sistema adesivo XP Bond. A degradação da interface por meio do armazenamento em água e ciclagem térmica não influenciou na resistência de união, independente do sistema adesivo empregado.
The aim of the present study was to survey the influence of endodontic irrigants on the adhesion resistance of adhesive systems to human dentin, after the degradation of adhesive interface and morphologic analysis of adhesive interface for Scanning Electronic Microscopy SEM. Sixty molar thirds were selected. The deep dentin was exposed removing and ground the oclusal portion. The specimens were irrigated with sodium hypochlorite 2,5% for 30 minutes followed by EDTA 17% for 5 minutes. Subsequently, teeth were divided randomly in six groups (n=10) accordingly to adhesive system applied: G1 and G2 Clearfil (Kuraray); G3 e G4 - Single Bond 2 (3M) e G5 e G6 - XP Bond (Dentsply). After adhesive system application, a composite resin Z100 (3M) was built up created. The degradation of the adhesive interface was realized by storage the specimens in deionized water and thermocycling: 24 hours of deionized water storage/no cycle (groups G1, G3 and G5) and 6 months storage in deionized water/12.000 cycles (groups G2, G4 and G6). After pre-established periods of each group, the systems tooth/resin were sectioned in order to obtain 4 sticks of approximately 1mm2, which were subjected to microtensile bond strength test. The morphologic analysis of interface was performed for SEM. Results were analyzed with ANOVA and Tukey test to level 5%. Significant difference between adhesives was verified (p<0,01). The water storage (6 months) coupled with thermocycling (12.000 cycles) did not affected significantly the resistance to microtensile bond strength of the dentin (p<0,05). The conclusion is that dentin irrigated with NaOCl and EDTA presented less resistance to microtensile bond strength when XP Bond Adhesive system was utilized. The interface degradation through water storage and thermocycling had no effect on the resistance of the dentin bond, independently of the adhesive system applied.

BARROS, Lívia de Oliveira. Estabilidade da interface de união de sistemas adesivos convencionais aplicados à dentina saturada com alcoóis. 2011. 50 f. Dissertação (Mestrado em Odontologia) - Faculdade de Farmácia, Odontologia e Enfermagem, Universidade Federal do Ceará, Fortaleza, 2011.
Submitted by denise santos (denise.santos@ufc.br) on 2015-10-21T15:16:50Z No. of bitstreams: 1 2011_dis_lobarros.pdf: 840593 bytes, checksum: bb384edc1f750fa69323f9aa3daf978b (MD5)
Approved for entry into archive by denise santos(denise.santos@ufc.br) on 2015-10-21T15:25:42Z (GMT) No. of bitstreams: 1 2011_dis_lobarros.pdf: 840593 bytes, checksum: bb384edc1f750fa69323f9aa3daf978b (MD5)
Made available in DSpace on 2015-10-21T15:25:42Z (GMT). No. of bitstreams: 1 2011_dis_lobarros.pdf: 840593 bytes, checksum: bb384edc1f750fa69323f9aa3daf978b (MD5) Previous issue date: 2011
There is a consensus that the resin-dentin bond instability is correlated with increased hydrophilic resin monomer content in dentin adhesive. Thus, more durable bonds could be created when more hydrophobic resins were used. One way to bond hydrophobic monomers to acid-etched dentin is saturating the demineralized dentin with ethanol instead of water (ethanol-wet bonding technique). The objective of this in vitro study was to evaluate the effect of “alcohol wet bonding” technique on the stability of adhesive interface produced by two-step etch-and-rinse adhesives systems. For this, it was used 20 human third molars that had superficial dentin exposed and were randomly divided into four experimental groups (n=5): Adper Single Bond 2 (SB) bonded to acid-etched dentin saturated with water or ethanol; and XP Bond (XP) bonded acid-etched dentin saturated with water or 99.5% tert-butanol. The simplified dentin dehydration protocol was performed using 2 μl 100% ethanol or 99.5% tert-butanol directly applied in dentin for 60 s. Composite build-ups were built on dentin surface and specimens were cut into non-trimming dentin-composite beams to microtensile testing. Beams from each tooth were divided equally in two subgroups: immediately tested and aged by immersion in 10% NaOCl solution for 1 h. Specimens were pulled until failure at crosshead speed of 1 mm/min and bond strength was calculated. Fractured sticks were analyzed and classified according to the failure mode as mixed, adhesive, cohesive in dentin and cohesive in composite; and expressed in percentage. Data from μTBS test were statistically analyzed using three-way ANOVA and Tukey tests (α=0.05). Additional dentin disks were bonded using the same groups tested and the morphological characteristics of adhesive interface were investigated by light microscopy after immersion in ammoniacal silver nitrate solution. μTBS results showed that NaOCl solution reduced significantly bond strength comparing with the control groups (p<0.05) and increased the silver nitrate interfacial deposit for all adhesives tested. SB used in ethanol saturated-dentin showed significant lower bond strength values in comparison with SB control group, and this same tendency was observed in the silver nitrate deposition. The use of tert-butanol did not influence XP bond strengths values and silver nitrate deposits. Conclusion: The “alcohol wet bonding” simplified technique used in the present study was not able to improve resin-dentin bond stability for simplified etch-and-rinse adhesive systems.
Existe um consenso de que a instabilidade da interface de união resina-dentina está relacionada com a quantidade de monômeros hidrofílicos presentes no sistema adesivo. Dessa forma, interfaces adesivas mais duradouras seriam alcançadas com a utilização de sistemas adesivos mais hidrofóbicos. Uma maneira de unir monômeros hidrófobos à dentina é através da saturação da matriz dentinária desmineralizada por etanol ao invés de água (ethanol-wet bonding technique). O objetivo deste trabalho in vitro foi avaliar o efeito do protocolo de saturação dentinária, utilizando alcoóis, na estabilidade da interface de união produzida por sistemas adesivos convencionais de dois passos. Para isso, foram utilizados 20 terceiros molares humanos, que tiveram a dentina coronária exposta e foram distribuídos aleatoriamente em quatro grupos experimentais (n=5): Adper Single Bond 2 (SB) aplicado sobre dentina saturada com água ou etanol; e XP Bond (XP) aplicado sobre dentina saturada com água ou tert-butanol. O protocolo de saturação da dentina foi realizado através da aplicação de 2 μl de etanol 100% ou tert-butanol 99,5% diretamente sobre a dentina por um período de 60 s. Um platô de resina composta foi confeccionado sobre superfície dentinária após a aplicação do sistema adesivo e os espécimes foram cortados pela técnica non-trimming de obtenção de palitos para o teste de microtração. Os palitos de cada dente foram igualmente divididos em dois subgrupos: imediatamente testado ou envelhecido em solução de NaOCl a 10% por 1 hora. Os espécimes foram tracionados até a ruptura da união a uma velocidade de 1 mm/min e sua força de união mensurada. Os palitos fraturados foram analisados e classificados de acordo com o modo de fratura em mista, adesiva, coesiva em dentina e coesiva em compósito, e os valores expressos em porcentagem. Os valores de resistência de união foram estatisticamente analisados usando os testes ANOVA a três critérios e Tukey (α=0.05). Discos extras de dentina foram submetidos aos procedimentos adesivos de cada grupo testado e utilizados para investigar as características morfológicas da interface de união através de microscopia óptica após imersão em solução amonical de nitrato de prata. Os resultados do teste de microtração mostraram que a imersão em solução de NaOCl reduziu significativamente a força de união em comparação aos grupos controle (p<0.05) e aumentou a nanoinfiltração das interfaces adesivas de todos os sistemas adesivos testados. A saturação da dentina com etanol 100% reduziu os valores de resistência adesiva para SB quando comparado ao grupo controle, e esta mesma tendência foi observada na infiltração de prata. O uso do tert-butanol 99,5% não afetou os valores de resistência adesiva para o XP, assim como a deposição de nitrato de prata na interface adesiva. Conclusão: Os protocolos simplificados de saturação da dentina com alcoóis utilizados no presente estudo não foram capazes de melhorar a estabilidade da interface de união para sistemas adesivos convencionais de dois passos.

Made available in DSpace on 2014-06-11T19:24:09Z (GMT). No. of bitstreams: 0 Previous issue date: 2004-12-07Bitstream added on 2014-06-13T18:51:45Z : No. of bitstreams: 1 farias_clc_me_arafo.pdf: 808344 bytes, checksum: 95ebf651344a3331fa67cd1e8c616f15 (MD5)
O objetivo deste trabalho foi avaliar, in vitro, os efeitos da desproteinização da dentina sobre a resistência de união de três diferentes sistemas adesivos. Para tal, 30 terceiros molares humanos hígidos foram seccionados transversalmente, por meio de disco diamantado, na união do terço médio com o terço oclusal e desgastados com discos de lixa de granulação 320 e 600 para completa exposição da superfície dentinária e padronização da smear layer. Em seguida, os dentes foram divididos aleatoriamente em 6 grupos (n=5), os quais receberam aplicação dos sistemas adesivos Prime & Bond 2.1 (Dentsply), Single Bond (3M) e Clearfil SE Bond (Kuraray) de acordo com as instruções dos fabricantes (Grupos 2, 4 e 6, respectivamente) ou após desproteinização da dentina com hipoclorito de sódio a 5% durante 2 minutos (Grupos 1, 3 e 5, respectivamente). Restaurações de resina composta Z100 foram confeccionadas, de forma incremental, sobre toda a superfície oclusal. Os dentes foram, então, seccionados com disco diamantado com a finalidade de obter amostras em forma de palitos de 1,0 l 0,2mm2 de área adesiva. Vinte e cinco amostras de cada grupo foram selecionadas e armazenadas por 24 horas em água destilada a temperatura de 37ºC. Em seguida, os testes de microtração foram realizados em Máquina Universal de Ensaios MTS, à velocidade do atuador de 0,5mm/min. Os resultados, analisados estatisticamente por meio de Análise de variância e Teste de Tukey (p<0,05), indicaram que a aplicação do NaOCl proporcionou redução da resistência adesiva para todos os grupos (G1- 29,16 l 3,98; G3- 23,06 l 4,87; G5- 26,71 l 5,10) quando comparados com os grupos controle (G2- 33,11 l 5,76; G4- 30,62 l 5,47; G6- 32,09 l 6,43). Em relação aos padrões de fratura, observou-se predominância de fraturas adesivas, sendo que estas, nos grupos onde a dentina foi... .
The aim of this study was to evaluate, in vitro, the influence of dentin deproteinization on microtensile bond strength of three different adhesive systems. Thirty freshly extracted human molars were transversely wetcut using a diamond disk in order to expose the oclusal dentin surface. The teeth were randomly divided into 6 groups (n=5) and the adhesive systems Prime & Bond 2.1 (Dentsply), Single Bond (3M) e Clearfil SE Bond (Kuraray) were applied according to the manufacturer's instruction (control groups: G2, G4 and G6) or after application of sodium hypochlorite 5% for 2 minutes (G1, G3 and G5). The teeth were restored with Z100 (3M) composite resin and the microtensile specimens, with a bonded area of 1,00l 0,2mm2, were prepared by a slow-speed diamond disk. Twenty-five specimens of each group were selected and stored in distilled-water at 37oC for 24 hours. The microtensile tests were performed in a MTS universal testing machine with a cross-head speed of 0,5mm/min. The results were statistically analyzed by ANOVA and Tukey's test (p=0,05). Sodium hypochlorite pre-treatment significantly decreased the microtensile bond strength values of all adhesive systems (G1- 29,16 l 3,98; G3- 23,06 l 4,87; G5- 26,71 l 5,10) compared to control groups (G2- 33,11 l 5,76; G4- 30,62 l 5,47; G6- 32,09 l 6,43). Analysis of the morphology of the failure pattern revealed that, for the control specimens, debonding had occurred in the composite/teeth interface and in specimens that were etched and deproteinized, debonding was characterized by resin failure through the wide bases of the tag extensions into dentinal tubules.

Orientador: Welingtom Dinelli
Banca: José Roberto Cury Saad
Banca: Silmara Aparecida Milori Corona
Resumo: O objetivo deste trabalho foi avaliar, in vitro, os efeitos da desproteinização da dentina sobre a resistência de união de três diferentes sistemas adesivos. Para tal, 30 terceiros molares humanos hígidos foram seccionados transversalmente, por meio de disco diamantado, na união do terço médio com o terço oclusal e desgastados com discos de lixa de granulação 320 e 600 para completa exposição da superfície dentinária e padronização da "smear layer". Em seguida, os dentes foram divididos aleatoriamente em 6 grupos (n=5), os quais receberam aplicação dos sistemas adesivos Prime & Bond 2.1 (Dentsply), Single Bond (3M) e Clearfil SE Bond (Kuraray) de acordo com as instruções dos fabricantes (Grupos 2, 4 e 6, respectivamente) ou após desproteinização da dentina com hipoclorito de sódio a 5% durante 2 minutos (Grupos 1, 3 e 5, respectivamente). Restaurações de resina composta Z100 foram confeccionadas, de forma incremental, sobre toda a superfície oclusal. Os dentes foram, então, seccionados com disco diamantado com a finalidade de obter amostras em forma de palitos de 1,0 l 0,2mm2 de área adesiva. Vinte e cinco amostras de cada grupo foram selecionadas e armazenadas por 24 horas em água destilada a temperatura de 37ºC. Em seguida, os testes de microtração foram realizados em Máquina Universal de Ensaios MTS, à velocidade do atuador de 0,5mm/min. Os resultados, analisados estatisticamente por meio de Análise de variância e Teste de Tukey (p<0,05), indicaram que a aplicação do NaOCl proporcionou redução da resistência adesiva para todos os grupos (G1- 29,16 l 3,98; G3- 23,06 l 4,87; G5- 26,71 l 5,10) quando comparados com os grupos controle (G2- 33,11 l 5,76; G4- 30,62 l 5,47; G6- 32,09 l 6,43). Em relação aos padrões de fratura, observou-se predominância de fraturas adesivas, sendo que estas, nos grupos onde a dentina foi... (Resumo completo, clicar acesso eletrônico abaixo).
Abstract: The aim of this study was to evaluate, in vitro, the influence of dentin deproteinization on microtensile bond strength of three different adhesive systems. Thirty freshly extracted human molars were transversely wetcut using a diamond disk in order to expose the oclusal dentin surface. The teeth were randomly divided into 6 groups (n=5) and the adhesive systems Prime & Bond 2.1 (Dentsply), Single Bond (3M) e Clearfil SE Bond (Kuraray) were applied according to the manufacturer's instruction (control groups: G2, G4 and G6) or after application of sodium hypochlorite 5% for 2 minutes (G1, G3 and G5). The teeth were restored with Z100 (3M) composite resin and the microtensile specimens, with a bonded area of 1,00l 0,2mm2, were prepared by a slow-speed diamond disk. Twenty-five specimens of each group were selected and stored in distilled-water at 37oC for 24 hours. The microtensile tests were performed in a MTS universal testing machine with a cross-head speed of 0,5mm/min. The results were statistically analyzed by ANOVA and Tukey's test (p=0,05). Sodium hypochlorite pre-treatment significantly decreased the microtensile bond strength values of all adhesive systems (G1- 29,16 l 3,98; G3- 23,06 l 4,87; G5- 26,71 l 5,10) compared to control groups (G2- 33,11 l 5,76; G4- 30,62 l 5,47; G6- 32,09 l 6,43). Analysis of the morphology of the failure pattern revealed that, for the control specimens, debonding had occurred in the composite/teeth interface and in specimens that were etched and deproteinized, debonding was characterized by resin failure through the wide bases of the tag extensions into dentinal tubules.
Mestre

Made available in DSpace on 2017-07-24T19:22:05Z (GMT). No. of bitstreams: 1 FABIANA SIQUEIRA.pdf: 4384235 bytes, checksum: 655ceab1a73a43f410cdb4b5e3773475 (MD5) Previous issue date: 2017-04-07
Coordenação de Aperfeiçoamento de Pessoal de Nível Superior
The aim of the present study was evaluate the adhesive properties of eroded dentin with different pH cycling using universal adhesive systems and to evaluate the application of collagen cross-linking agent or MMP inhibitors on the resin-eroded dentin interface, through of three in vitro studies. For the experiment 1, the teeth were randomly assigned into the experimental groups according to the combination of variables: dentin surface (sound dentin and eroded dentin) vs adhesive systems (10 universal adhesives) vs Adhesive strategy [etch-and-rinse (ER) and self-etch (SE)]. The adhesive systems were applied according to the manufacturer's instructions and the teeth were restored. They were sectioned to analysis of microtensile bond strength (μTBS) and nanoleakage (NL). The surfaces of 2 tooth were examined under scanning electron microscopy (SEM) to evaluate the surface characterization after erosive-cycling. For experiment 2, the teeth were randomly assigned into 18 experimental conditions according to the variables: Erosive cycling (eroded dentin with soft drink pH ≈ 2,7 and eroded dentin with citric acid pH 2.3) vs. adhesive systems [Prime & Bond Elect (PBE); Scotchbond Universal Adhesive (SBU); Tetric N-Bond Universal (TEU)] vs Treatment agents [6.5% primer containing proanthocyanidin (PA) and 0.1% riboflavin (RI)]. The surface was treated with primers and the adhesive systems were applied and restored. The samples were sectioned and tested for μTBS, NL and degree of conversion (DC). The surfaces of 2 tooth were examined under SEM to evaluate the surface characterization after erosive-cycling. For experiment 3, the teeth were randomly assigned into 18 experimental conditions according to the variables: Erosive cycling (eroded dentin with soft drink pH ≈ 2,7 and eroded eroded with citric acid pH 2.3) vs. Adhesive Systems (PBE; SBU; TEU) vs Acid pretreatment [control with 37% phosphoric acid;Phosphoric acid containing 2% chlorhexidine (CHXacid) and phosphoric acid containing 3% PA (PAacid)]. The teeth were acid-etched according to each experimental conditions, the adhesive systems were applied and the teeth were restored. The teeth were sectioned and tested for μTBS, NL and DC. Data were submitted to appropriate statistical analysis (α = 0.05). The μTBS values in eroded dentin were statistically lower than sound dentin, independent of the adhesive strategy (p < 0.01) The inclusion of primers containing collagen cross-linking agents in the eroded dentin adhesive protocol improved μTBS values (p <0.001),significantly reduced NL (p <0.004) for all the adhesives tested, as well as improved DC (p <0.03). The use of phosphoric acids containing MMPs inhibitors or collagen cross-linking agent improved μTBS values (p> 0.33), produced a significant reduction of NL (p <0.004) and improved DC (p <0.03). The application of MMP inhibitors (primer or acid etching - containing) were effective to improve the properties of the resin-eroded dentin interface.
O objetivo desse estudo foi avaliar as propriedades adesivas à dentina erosionada utilizando sistemas adesivos universais e verificar o efeito da aplicação de agentes reticuladores de colágeno ou inibidores de Metaloproteinases (MMPs) na interface resina-dentina erosionada, através de três estudos laboratoriais. Para o experimento 1, os dentes foram distribuídos aleatoriamente entre os grupos experimentais de acordo com a combinação das variáveis: superfície dentinária (controle sem erosão e erosionada) vs. sistemas adesivos (10 sistemas adesivos universais) vs.estratégia adesiva [condicionamento convencional (ER) e autocondicionante (SE)].Os sistemas adesivos foram aplicados de acordo com as especificações do fabricante e os dentes foram restaurados. Depois foram seccionados para análise da resistência de união à dentina (μTBS) e nanoinfiltração (NI). A superfície de 2 dentes foi examinada sob microscopia eletrônica de varredura (MEV) para avaliar as características da superfície após ciclagem erosiva. Para o experimento 2, os dentes foram aleatoriamente alocados em 18 condições experimentais de acordo com as variáveis: Ciclagem erosiva (dentina erosionada com coca-cola pH ≈ 2,7 e dentina erosionada com ácido cítrico pH 2,3) vs. Sistemas adesivos [Prime & Bond Elect (PBE), Scotchbond Universal Adhesive (SBU) e Tetric N-Bond Universal (TEU)] vs. Agentes de tratamento [primer contendo 6,5% de roantocianidina (PA) e primer contendo 0,1% de riboflavina (RI)]. Os sistemas adesivos foram aplicados de acordo com as especificações do fabricante após aplicação do primer e restaurados. A seguir, os dentes foram seccionados e testados para análise da μTBS, NI e grau de conversão (GC). A superfície de 2 dentes foi examinada sob MEV para avaliar as características da superfície após erosão. Para o experimento 3, os dentes foram alocados aleatoriamente dentro de 18 condições experimentais de acordo com as variáveis: Ciclagem erosiva (dentina erosionada com coca-cola pH ≈ 2,7 e dentina erosionada com ácido cítrico pH 2,3) vs. Sistemas adesivos (PBE, SBU e TEU) vs. pré-tratamento ácido [controle com ácido fosfórico 37%; Ácido fosfórico contendo 2% de clorexidina (CHXacido) e ácido fosfórico contendo 3% de PA (PAacido)]. Os dentes foram condicionados de acordo com cada grupo experimental, os sistemas adesivos foram aplicados e restaurados com resina composta. Posteriormente, os dentes foram seccionados e testados para análise da μTBS, NI e GC. Todos os dados foram submetidos a ANOVA 3 fatores e teste de Tukey (α = 0,05). Os valores de μTBS em dentina erosionada foi estatisticamente inferior à dentina sadia,independente da estratégia adesiva (p > 0,61). A inclusão de primers contendo agentes reticuladores de colágeno no protocolo adesivo a dentina erosionada,melhorou os valores de μTBS (p < 0,001), diminuiu significativamente a NI (p <0,004) para os adesivos testados, além de melhorar o GC (p < 0,03). A utilização de ácidos fosfórico contendo inibidores de MMPs ou agentes reticuladores de colágeno melhorou os valores de μTBS (p > 0,33), produziu uma redução significativa da NI (p < 0,004) e melhorou o GC (p < 0,03). Os agentes reticuladores independente do veículo (primer ou condicionamento ácido) foram eficazes para melhorar as propriedades da interface resina-dentina erosionada.

Submitted by Eunice Novais (enovais@uepg.br) on 2018-09-11T14:03:43Z No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) Taise Hanzen.pdf: 2068610 bytes, checksum: 63860393bd79b5a0ebafdc98b4fd73e2 (MD5)
Made available in DSpace on 2018-09-11T14:03:43Z (GMT). No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) Taise Hanzen.pdf: 2068610 bytes, checksum: 63860393bd79b5a0ebafdc98b4fd73e2 (MD5) Previous issue date: 2018-02-20
O propósito deste estudo in vitro foi avaliar o efeito da adição de nanopartículas de cobre em um sistema adesivo universal sobre a resistência de união (RU) e nanoinfiltração (NI) da interface resina-dentina hígida, erosionada e cariada, nas estratégias adesivas convencional (total-etch [TE]) e autocondicionante (self-etch [SE]). Bem como grau de conversão (GC), morfologia da interface de união (MI), resistência máxima à tração (RT), sorção cumulativa de água (SO) e solubilidade (SB) do sistema adesivo e radiopacidade do cobre (RC). O sistema adesivo experimental foi formulado com a adição de nanopartículas de cobre a 0,1% no adesivo Ambar Universal. Para os testes de RU e NI, 120 molares humanos foram aleatoriamente distribuídos em doze condições experimentais (n = 10) com base na combinação das variáveis: concentração de cobre [0 e 0,1%] vs. superfície dentinária (hígida, erosionada e cariada) vs. estratégias adesivas (TE e SE). Aplicado o sistema adesivo, os dentes foram restaurados com resina composta e após 24h, seccionados longitudinalmente para se obter palitos de resina-dentina (0,8 mm2), testados em tensão a 0,5 mm/min quanto a RU. Para NI, 3 palitos de cada dente foram preparados e analisados em microscopia eletrônica de varredura (MEV). Para avaliação do GC, 3 palitos de resina-dentina de cada condição experimental foram analisados por espectroscopia Raman. Para MI, 3 palitos de resina-dentina foram preparados e analisados por FEG. Para RT, 5 corpos de prova de adesivo de cada condição experimental foram testados nos tempos imediato (24h) e após 28 dias de armazenamento (n = 10). Para SO e SB, 10 corpos de prova de adesivo (n=10) de cada condição experimental foram testados durante o período de 56 dias. Para avaliação da RC, 5 corpos de prova de cada condição experimental (n = 5) foram submetidos a 5 radiografias digitais, para comparação em escala de cinza. Os dados de RU, NI e GC foram analisados por ANOVA 3 fatores, submetidos ao teste post-hoc de Tukey para múltiplas comparações. Para RT, os dados foram analisados por ANOVA 2 fatores para medidas repetidas. Os dados de RC foram analisados por ANOVA fator único. Os dados de SO e SB foram submetidos à análise por test-t pareado. A significância estatística foi predefinida em 5%. A inclusão de nanopartículas de cobre na concentração 0,1% no sistema adesivo universal aumentou os valores de RU sobre os substratos hígido e erosionado. O adesivo contendo cobre melhorou a NI no substrato hígido, em ambas as estratégias. Para RT, RC, SO e SB, a adição de cobre não apresentou diferenças estatísticas. O GC foi mais afetado em substrato erosionado quando na técnica convencional associada ao adesivo contendo cobre, que resultou na formação de tags menores e em quantidade reduzida.
The purpose of this in vitro study was to evaluate the effect of addition of copper nanoparticles on a universal adhesive system in microtensile bond strength (μTBS) and nanoleakage (NL) of sound, eroded and carious resin-dentin interface, using both self-etch [SE] and total-etch [TE] adhesive strategies. As well as degree of conversion (DC), interface micromorphology (IM), ultimate tensile strength (UTS), cumulative water sorption (WS) and solubility (So) of the adhesive system and copper radiopacity (CR). The experimental adhesive system was formulated with the addition of 0,1% copper nanoparticles on Ambar Universal. For μTBS and NL, 120 human third molars were randomly distributed in 12 experimental conditions (n=10) based on the combination of the variables: concentration of copper [0 and 0,1%] vs. dentin surface (sound, eroded and carious) vs. adhesive strategies (TE and SE). After bonding procedures and restored with composite resin, teeth were stored for 24h and then longitudinally sectioned to obtain specimens – dentin-resin sticks (0,8mm2), tested in a tension of 0,5mm/min for μTBS. For NL, 3 specimens per tooth were prepared and analyzed by scanning electron microscopy (SEM). For DC, 3 sticks of resin-dentin of each experimental condition were analyzed by Raman spectroscopy. For IM, 3 sticks of resin-dentin were prepared and analyzed by FEG. For UTS, 5 samples of each condition were tested after 24 hours and 28 days of storage (n = 10). For WS and So, 10 samples of each experimental condition (n = 10) were tested during 56 days. For radiopacity, 5 CPAs of each experimental condition (n = 5) were submitted to 5 digital radiographs, for comparison in gray scale in Adobe Photoshop Software. The data of μTBS, NL and DC (Raman) were analyzed by three-way ANOVA, submitted to Tukey's post hoc test for multiple comparisons. For UTS, data were analyzed by two-way ANOVA. For CR, data were analyzed by one-way ANOVA. The data of WS and So were evaluated by Student’s T-test. Statistical significance was set at α = 0.05. The inclusion of 0,1% of copper nanoparticles on the universal adhesive system improved μTBS values on sound and eroded substrates. The copper adhesive improved NL on sound dentin, for both strategies. For UTS, radiopacity, WS and So, the addition of copper showed no statistical difference in the results. DC was most affected by eroded dentin associated with ER strategy and adhesive containing copper, which resulted in smaller tags, in reduced quantity.

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde. Programa de Pós-Graduação em Odontologia
Made available in DSpace on 2012-10-21T07:33:40Z (GMT). No. of bitstreams: 1 199923.pdf: 5142658 bytes, checksum: 3466433c0cd7caf76def23c5a1ef63ea (MD5)

2013/2014
Restorative adhesive dentistry is based on the infiltration of dental adhesive resin within the dentin collagen network creating the hybrid layer. The stability and integrity of collagen fibrils within the hybrid layer are crucial for the maintenance of bond effectiveness over time. The matrix metallo-proteinases enzymes (MMPs), which are endogenous enzymes present in dentin tissue, are claimed to play a key role in affecting the integrity of the hybrid layer causing the hydrolysis and degradation of dentin collagen. The aim of this research project was to evaluate the efficacy of different cross-linking agent in preserving the adhesive/dentin layer. Two water soluble collagen cross-linking agents riboflavin, and the carbodiimide hydrochloride, 1-ethyl-3-[3-dimethylaminopropyl] (EDC) were initially tested, then additional cross-linking agents were included in the study: acrolein, (water soluble), and the N,N'-dicyclohexylcarbodiimide (DCC) (soluble in acetone and ethanol). The concentration of each solution was chosen according to the previous studies: 0.1% riboflavin/wt, 0.3M EDC/wt, 0,01% acrolein/wt, 0.5M DCC/ethanol, 0.5M/acetone. Cross-linkers were associated to different adhesive systems available on the market and different tests were performed to evaluate the ability of cross-linkers in preserving the hybrid layer: mechanical test (microtensile bond strength), qualitative test (nanoleakage analysis), and biochemical assays (zymographic analysis and in situ zymographic analysis). For the microtensile bond strength recently extracted third molars (N=5 for each group) were selected and restorative treatments were performed: in the experimental groups teeth were pretreated with the tested cross-linkers before the application of the adhesive systems (XP Bond, Scotch Bond 1XT, Optibond FL, Clearfil SE), while in the control groups the adhesives were applied according to the manufacturers’ instructions. The experimental groups were divided as follow: 1) 0.1% riboflavin/XP Bond; 0.3M EDC/Scotch Bond 1XT; 2) 0.3M EDC+XP Bond 3) 0.3M EDC+Scotch Bond 1XT; 4) 0.3M EDC+Optibond FL; 5) 0.01% acrolein+Scotch Bond 1XT; 6) 0.3M EDC+Clearfil SE. The bonded specimens were serially sectioned to obtain approximately 1-mm-thick beams in accordance with the microtensile non-trimming technique. Beams were stored at 37°C in artificial saliva to reproduce the oral cavity environment and then were stressed to failure after 24hours (T0), 6 months (T6) or 1 year (T12) using a simplified universal testing machine at a crosshead speed of 1 mm/min. Data were analyzed using Two-Way (variables: cross-linker pretreatment and storage time) analysis of variance (ANOVA) and post hoc Tukey test (p values < 0.05 were considered as statistically significant). The results of microtensile bond strength showed that the use of the tested cross-linkers tested does not affect the immediate bond strength, while at T12 bond strength values of the experimental groups are significantly higher compared to the control groups. For the qualitative interfacial nanoleakage analysis, additional molars (4 per group) were selected to evaluate the integrity of the tooth/resin interfaces. The experimental groups were divided as follow: 1) 0.1% riboflavin-XP Bond; 2) 0.3M EDC-Scotch Bond 1XT; 3) 0.3M EDC-Optibond FL. The specimens were prepared and stored as described for the microtensile test; after storage the beams were immersed for 24h in AgNO3, then rinsed in distilled water and immersed in photo-developing solution to reduce silver ions into metallic silver grain. Nanoleakage analysis was performed under light microscopy and the interfacial nanoleakage degree was scored on a scale of 0–4 based on the percentage of the adhesive surface showing silver nitrate deposition: 0: no nanoleakage; 1: <25% nanoleakage; 2: 25 to ≤50% nanoleakage; 3: 50 to ≤75% nanoleakage; and 4: >75% nanoleakage. Statistical differences among nanoleakage group scores were analyzed using the χ2 test. The results did not reveal differences in the interfacial nanoleakage expression between the experimental groups 2 (0.3M EDC-Scotch Bond 1XT) and 3 (0.3M EDC-Optibond FL) and their respective control group. After 12-month storage the treatment with the riboflavin significantly reduce the infiltration of AgNO3 within the hybrid layer created with XP Bond. For the biochemical assay of the enzymatic activity, zymographic analysis and in situ zymography were performed. The following groups were added to the previously described treatments and submitted to these tests: 0.5M DCC/ethanol, 0.5M DCC/acetone, 0.5M DCC/ethanol- Scotchbond 1XT, 0.5M DCC/acetone Scotchbond 1XT. For the zymographic analysis dentin powder was obtained from thirty human sound molars; the powder was treated with the cross-linking agents in association or not with the different adhesive systems. The extract proteins were submitted to electrophoresis on SDS-polyacrylamide gels copolymerized with gelatin as MMPs substrate. Zymograms showed that the use of cross-linkers before the adhesive application was able to reduce or totally inhibit the activity of MMPs (especially MMP-2 and MMP-9). The specimens submitted to in situ zymography were prepared as previous described for the microtensile test. Bonded specimens were cut in order to expose the adhesive/dentin interfaces and in situ zymography was performed applying a self-quenched fluorescein-conjugated gelatin on adhesive/dentin interface. The specimens were light-protected and incubated in humidified chambers at 37°C for 24 h, then the hydrolysis of quenched fluorescein-conjugated gelatin substrate (related to endogenous gelatinolytic enzyme activity) was assessed by examination with a confocal laser scanning microscope. Images revealed reduced green fluorescence in the hybrid layer of experimental groups (pretreated with the cross-linking agents) compared to the control group fluorescence. The results of all these studies suggest that the use of cross-linking agents before the bonding procedures improves the stability of the resin/dentin interface. We can speculated that cross-linkers are able to reinforced the dentin collagen network increasing the mechanical properties of the hybrid layer, as confirmed by the microtensile test. Furthermore the results showed that these agents are able to inhibit the MMP gelatinolytic activity, preserving the dentin collagen fibrils from the hydrolysis and avoiding the failure of the hybrid layer.
L’odontoiatria adesiva si basa sulla capacità delle resine adesive di penetrare all’interno del network del collagene dentinale portando alla formazione del cosiddetto strato ibrido; la stabilità e l’integrità delle fibrille collagene dello strato ibrido sono fondamentali per preservare le caratteristiche dell’adesione al tessuto dentinale nel tempo. È noto che le metallo-proteinasi della matrice (MMPs), enzimi endogeni della dentina, possono causare l’idrolisi e la conseguente degradazione dello strato ibrido dentinale. Scopo del presente progetto di ricerca è stata la valutazione dell’efficacia di diversi agenti cross-linkers del collagene sulla stabilità dell’interfaccia adesivo/dentinale. Inizialmente sono stati testati due diversi agenti cross-linkers, entrambi solubili in acqua: la riboflavina ed il carbodiimide hydrochloride, 1-Ethyl-3-[3-dimethylaminopropyl] (EDC), successivamente sono state incluse nello studio altre due sostanze: l’acroleina (solubile in acqua), e il N,N'-dicyclohexylcarbodiimide (DCC) (solubile in etanolo o acetone). La concentrazione di ogni soluzione testata è stata scelta in accordo con la letteratura: 0.1% riboflavina/wt, 0.3M EDC/wt, 0,01% acroleina/wt, 0.5M DCC/etanolo, 0.5M/acetone. Gli agenti cross-linkers sono stati testati in associazione a diversi sistemi adesivi disponibili sul mercato. Al fine di valutarne la capacità nella conservazione dello strato ibrido sono state scelte diverse tipologie di analisi: meccanica (microtensile bond strength), qualitativa (analisi del nanoleakage), e biochimiche (zimografia e zimografia in situ). L’analisi meccanica è stata effettuata mediante il test del microtensile per il quale sono stati scelti denti molari umani (5 per gruppo) su cui sono state effettuate le procedure per un restauro adesivo: nei gruppi sperimentali la dentina è stata trattata con l’agente cross-linker scelto prima dell’applicazione del sistema adesivo; nei gruppi controllo gli adesivi (XP Bond, Scotch Bond 1XT, Optibond FL, Clearfil SE) sono stati utilizzati seguendo le istruzioni del produttore. I gruppi sperimentali sono stati suddivisi nel seguente modo: 1) 0.1% riboflavina+XP Bond; 0.3M EDC+Scotch Bond 1XT; 2) 0.3M EDC+XP Bond 3) 0.3M EDC+ScotchBond 1XT; 4) 0.3M EDC+Optibond FL; 5) 0.01% acrolein+ScotchBond 1XT; 6) 0.3M EDC+Clearfil SE. I campioni sono stati poi tagliati per ottenere sticks delle dimensioni di 1 mm circa di spessore in accordo con la “non-trimming technique”. I campioni ottenuti sono stati conservati, in saliva artificiale a 37°C per simulare l’ambiente del cavo orale. Dopo 24 ore (T0), 6 mesi (T6), e 1 anno (T12) i campioni sono stati sottoposti a test di trazione usando una macchina universale alla velocità di 1 mm/min. I dati sono stati analizzati con il test di ANOVA a due vie (trattamento con il cross-linker/tempo di storaggio) e con il post hoc Tukey test (valori di p < 0.05 indicano differenza statisticamente significativa). I risultati del test di microtensile hanno mostrato che il pretrattamento con cross-linkers del collagene non influisce sui valori di adesione a T0, mentre i valori a T12 evidenziano che l’uso dei cross-linkers aumenta significativamente l’adesione rispetto ai rispettivi gruppi controllo. L’analisi qualitativa dell’interfaccia adesiva è stata effettuata mediante valutazione del nanoleakage. A tale scopo, sono stati aggiunti altri 4 molari per ciascun gruppo. I gruppi sperimentali sono stati divisi come segue: 1) 0.1% riboflavina+XP Bond; 2) 0.3M EDC+Scotch Bond 1XT; 3) 0.3M EDC+Optibond FL. I campioni sono stati preparati come precedentemente descritto per il test di microtensile e dopo i medesimi tempi di storaggio i campioni sono stati immersi in una soluzione acquosa di nitrato di argento (AgNO3) per 24 ore, sciacquati, e successivamente immersi in liquido di sviluppo al fine di ridurre gli ioni di argento. I campioni sono stati quindi analizzati al microscopio ottico, ed il nanoleakage è stato quantificato con valori da 0 a 4, basandosi sulla percentuale di superficie dello strato ibrido infiltrata dal nitrato d’argento, come segue: 1: <25% nanoleakage; 2: 25 a ≤50% nanoleakage; 3: 50 a ≤75% nanoleakage; and 4: >75% nanoleakage. I dati sono stati analizzati utilizzando il χ2 test. I risultati mostrano differenze significative a T12 solo per il gruppo 1 (0.1% riboflavina-XP Bond), in cui il gruppo sperimentale trattato con agente cross-linkers presenta all’interno dello strato ibrido una minore quantità di AgNO3 se comparato al gruppo controllo. Al contrario gli altri due cross-linkers presi in analisi non hanno mostrato differenze statisticamente significative in relazione al loro uso a T0 o T12. In relazione ai tests biochimici, sono state effettuati test si zimografia e la zimografia in situ al fine di valutare l’attività enzimatica delle MMPs dentinali in relazione al trattamento con agenti cross-linkers. Ai gruppi precedentemente testati sono stati aggiunti ulteriori 4 gruppi sperimentali: 0.5M DCC/etanolo, 0.5M DCC/acetone, 0.5M DCC/etanolo-Scotchbond 1XT, 0.5M DCC/acetone-Scotchbond 1XT. Per la zimografia sono stati scelti trenta molari sani dai quali è stata isolata la dentina e polverizzata. La polvere di dentina è poi stata trattata con i diversi cross-linkers e adesivi come precedentemente descritto. Le proteine estratte dalla polvere dentinale, trattata secondo i diversi gruppi di appartenenza, sono state quindi sottoposte a corsa elettroforetica su gel di SDS-page co-polimerizzato con gelatina, come substrato delle MMPs. I gels ottenuti mostrano che il trattamento della dentina con agenti cross-linker prima dell’applicazione degli adesivi dentinali è in grado di diminuire o inibire quasi completamente l’attività gelatinolitica delle MMPs (MMP-2 -9 in particolare). Per quanto riguarda la zimografia in situ i campioni sono stati preparati come descritto per il test di microtensile, successivamente sono stati tagliati in modo da esporre l’interfaccia adesiva. A livello della stessa interfaccia è stata posta della gelatina coniugata con fluorescina. L’idrolisi della gelatina causata dagli enzimi endogeni dentinali determina l’attivazione della fluorescenza evidenziando quindi in situ l’attività enzimatica. I campioni sono stati osservati mediante microscopio confocale ed hanno evidenziato una minore fluorescenza all’interno dello strato ibrido di tutti gruppi sperimentali presi in analisi se confrontate con i rispettivi gruppi controllo. In conclusione possiamo affermare che l’uso degli agenti cross-linkers del collagene prima delle procedure adesive migliora le caratteristiche generali dello strato ibrido. È possibile suppore che i cross-linkers siano in grado di rinforzare il network del collagene dentinale aumentandone le proprietà meccaniche, come dimostrato dal test del microtensile; inoltre i tests enzimatici mostrano come questi agenti siano in grado di inibire l’attività enzimatica delle MMPs preservando in questo modo l’idrolisi delle fibrille collagene ed evitando la conseguente disgregazione dello strato ibrido.
XXVII Ciclo
1986

Made available in DSpace on 2014-06-11T19:31:25Z (GMT). No. of bitstreams: 0 Previous issue date: 2013-08-13Bitstream added on 2014-06-13T19:20:23Z : No. of bitstreams: 1 000757509.pdf: 3603402 bytes, checksum: 16b2be7b7c8255899a8ded28ec457d93 (MD5)
O objetivo deste estudo foi avaliar a resistência de união dos sistemas adesivos Clearfil SE Bond (CL) e Single Bond (SB) ao esmalte e dentina, em função da associação ou não do Nd:YAG Laser e do tempo de armazenagem (24 h e 12 meses). Foram utilizados 240 dentes bovinos com superfícies de esmalte ou dentina planificadas, que foram divididos em 4 grupos (n = 15) para cada substrato, de acordo com o sistema adesivo e a técnica: G1 (Controle) - CL + fotopolimerização; G2 (Controle) - SB + fotopolimerização; G3 (Experimental/Laser) - CL + Nd:YAG Laser + fotopolimerização; G4 (Experimental/Laser) - SB + Nd:YAG Laser + fotopolimerização. Para o esmalte, foi utilizada a densidade de energia = 174,16 J/cm2 e, para a dentina, a densidade de energia = 149,28 J/cm2 do Nd:YAG Laser. Foram confeccionadas restaurações de resina composta Z-350. Após armazenagem de 24 h ou 12 meses em água destilada à 37º C, foram realizadas as secções nos dentes para obtenção de amostras com área adesiva de aproximadamente 1 mm2, seguido de teste de microtração. Para cada substrato, foi realizado o teste estatístico ANOVA três fatores (Sistema adesivo X Técnica X Tempo de armazenagem), seguido do Teste de Tukey (α = 5%). Foi realizada MEV para análise complementar da interface adesiva. Para o esmalte, foram observadas diferenças significantes para a interação entre Tipo de adesivo X Técnica e Técnica X Tempo de armazenagem. Os valores de média em MPa (±Desvio-padrão) para a interação entre Tipo de adesivo X Técnica: SB/Controle = 35,78 (± 6,04)a; SB/Laser = 26,40 (± 7,25)b; CL/Controle = 26,32 (± 5,71)b; CL/Laser = 23,90 (± 7,49)b. Os valores de média em MPa (±Desvio-padrão) para a interação entre Técnica X Tempo de armazenagem: Controle/24h = 32,58 (± 6,49)a; Controle/12 meses = 29,52 (± 8,38)a; Laser/24h = 29,37 (± 5,71)a; Laser/12 meses = 20,92 (± 6,5)b. Para...
The aim of this study was to evaluate the bond strength of Clearfil SE Bond (CL) and Single Bond (SB) adhesive systems to enamel and dentin, depending on whether association with Nd: YAG Laser and storage time (24 h and 12 months). A total of 240 bovine teeth with enamel or dentin surfaces planned were prepared, which were divided into 4 groups (n = 15) for each substrate, according to the adhesive system and technique: G1 (control) - CL + photopolymerization; G2 (Control) - SB + photopolymerization; G3 (Experimental/Laser) - CL + Nd: YAG Laser + photopolymerization; G4 (Experimental/Laser) - SB + Nd: YAG Laser + photopolymerization. To the enamel, was used energy density = 174.16 J/cm2 and for dentine, energy density = 149.28 J/cm2 of Nd: YAG Laser. Composite restorations were fabricated (Filtek Z-350). After storage for 24 h or 12 months in distilled water at 37 ° C, the sections were performed on teeth to obtainment sticks with an area of about 1 mm2 adhesive interface, followed by microtensile test. For each substrate, we performed a three-way ANOVA (adhesive X Technical X Storage time), followed by the Tukey test (α = 5%). SEM analysis was performed to supplement the adhesive interface. For enamel, significant differences were observed for interaction factors Adhesive X Technique and Technique X Storage time. The mean values in MPa (± standard deviation) for interaction factor Adhesive X Technique: SB / Control = 35.78 (± 6.04) a; SB / Laser = 26.40 (± 7.25) b, CL / Control = 26.32 (± 5.71) b, CL / Laser = 23.90 (± 7.49) b. The mean values in MPa (± standard deviation) for interaction factor Technique X Storage time: Control/24h = 32.58 (± 6.49)a; Control/12 months = 29.52 (± 8.38 )a; Laser/24h = 29.37 (± 5.71)a; Laser/12 months = 20.92 (± 6.5)b. For dentin, significant differences were observed for interaction factors Technique X Storage time and Adhesive X Technique ...

Orientador: Sérgio Eduardo de Paiva Gonçalves
Banca: César Rogério Pucci
Banca: Ricardo Scarparo Navarro
Banca: Alessandra Nara de Souza Rastelli
Banca: Maria Filomena Rocha Lima Huhtala
Resumo: O objetivo deste estudo foi avaliar a resistência de união dos sistemas adesivos Clearfil SE Bond (CL) e Single Bond (SB) ao esmalte e dentina, em função da associação ou não do Nd:YAG Laser e do tempo de armazenagem (24 h e 12 meses). Foram utilizados 240 dentes bovinos com superfícies de esmalte ou dentina planificadas, que foram divididos em 4 grupos (n = 15) para cada substrato, de acordo com o sistema adesivo e a técnica: G1 (Controle) - CL + fotopolimerização; G2 (Controle) - SB + fotopolimerização; G3 (Experimental/Laser) - CL + Nd:YAG Laser + fotopolimerização; G4 (Experimental/Laser) - SB + Nd:YAG Laser + fotopolimerização. Para o esmalte, foi utilizada a densidade de energia = 174,16 J/cm2 e, para a dentina, a densidade de energia = 149,28 J/cm2 do Nd:YAG Laser. Foram confeccionadas restaurações de resina composta Z-350. Após armazenagem de 24 h ou 12 meses em água destilada à 37º C, foram realizadas as secções nos dentes para obtenção de amostras com área adesiva de aproximadamente 1 mm2, seguido de teste de microtração. Para cada substrato, foi realizado o teste estatístico ANOVA três fatores (Sistema adesivo X Técnica X Tempo de armazenagem), seguido do Teste de Tukey (α = 5%). Foi realizada MEV para análise complementar da interface adesiva. Para o esmalte, foram observadas diferenças significantes para a interação entre Tipo de adesivo X Técnica e Técnica X Tempo de armazenagem. Os valores de média em MPa (±Desvio-padrão) para a interação entre Tipo de adesivo X Técnica: SB/Controle = 35,78 (± 6,04)a; SB/Laser = 26,40 (± 7,25)b; CL/Controle = 26,32 (± 5,71)b; CL/Laser = 23,90 (± 7,49)b. Os valores de média em MPa (±Desvio-padrão) para a interação entre Técnica X Tempo de armazenagem: Controle/24h = 32,58 (± 6,49)a; Controle/12 meses = 29,52 (± 8,38)a; Laser/24h = 29,37 (± 5,71)a; Laser/12 meses = 20,92 (± 6,5)b. Para...
Abstract: The aim of this study was to evaluate the bond strength of Clearfil SE Bond (CL) and Single Bond (SB) adhesive systems to enamel and dentin, depending on whether association with Nd: YAG Laser and storage time (24 h and 12 months). A total of 240 bovine teeth with enamel or dentin surfaces planned were prepared, which were divided into 4 groups (n = 15) for each substrate, according to the adhesive system and technique: G1 (control) - CL + photopolymerization; G2 (Control) - SB + photopolymerization; G3 (Experimental/Laser) - CL + Nd: YAG Laser + photopolymerization; G4 (Experimental/Laser) - SB + Nd: YAG Laser + photopolymerization. To the enamel, was used energy density = 174.16 J/cm2 and for dentine, energy density = 149.28 J/cm2 of Nd: YAG Laser. Composite restorations were fabricated (Filtek Z-350). After storage for 24 h or 12 months in distilled water at 37 ° C, the sections were performed on teeth to obtainment sticks with an area of about 1 mm2 adhesive interface, followed by microtensile test. For each substrate, we performed a three-way ANOVA (adhesive X Technical X Storage time), followed by the Tukey test (α = 5%). SEM analysis was performed to supplement the adhesive interface. For enamel, significant differences were observed for interaction factors Adhesive X Technique and Technique X Storage time. The mean values in MPa (± standard deviation) for interaction factor Adhesive X Technique: SB / Control = 35.78 (± 6.04) a; SB / Laser = 26.40 (± 7.25) b, CL / Control = 26.32 (± 5.71) b, CL / Laser = 23.90 (± 7.49) b. The mean values in MPa (± standard deviation) for interaction factor Technique X Storage time: Control/24h = 32.58 (± 6.49)a; Control/12 months = 29.52 (± 8.38 )a; Laser/24h = 29.37 (± 5.71)a; Laser/12 months = 20.92 (± 6.5)b. For dentin, significant differences were observed for interaction factors Technique X Storage time and Adhesive X Technique ...
Doutor

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2014.
Made available in DSpace on 2014-08-06T18:02:16Z (GMT). No. of bitstreams: 1 326596.pdf: 70286873 bytes, checksum: 1a3f6a5a37119122f45b0181d91a596e (MD5) Previous issue date: 2014
Objetivos: Este estudo teve como objetivo avaliar a resistência de união sob teste de microtração ao esmalte clareado utilizando diferentes sistemas adesivos após o tratamento clareador. Material e métodos: Para isso utilizou-se a face vestibular de 30 incisivos bovinos, que foram divididos em 6 grupos: em G1, G2 e G3 não submetidos ao clareamento e G4, G5 e G6 submetidos ao clareamento com peróxido de carbamida 10% (Power Bleaching, BM4) por 1 mês (2 h/dia). Em seguida os dentes foram restaurados com resina composta utilizando os seguintes sistemas adesivos: em G1 e G4 utilizou-se o adesivo Prime&Bond; enquanto em G2 e G5 Gluma2; já em G3 e G6 o adesivo Clearfill SE BOND, sendo escolhidos com base no solvente. Após 24 horas armazenados em água, obtiveram-se palitos (0,9 mm2) através de cortes seriais e transversais, e submetidos ao teste de microtração (0,5 mm/s). Resultados: A análise estatística demonstrou diferença significante da resistência de união entre o esmalte clareado e não clareado. Além disso, o adesivo Prime&Bond mostrou resistência de união média superior aos demais adesivos. A análise da interação entre o tratamento de superfície e o adesivo utilizado mostrou maior resistência adesiva em esmalte não clareado em Prime&Bond e Gluma2. Entretanto, Gluma2 obteve os valores mais baixos no esmalte clareado. Prime&Bond e Clearfill SE BOND apresentaram valores semelhantes em esmalte clareado, sendo que Clearfill SE BOND não obteve diferença quando comparado o esmalte clareado ao não clareado. Conclusão: O tratamento clareador influenciou negativamente a resistência adesiva à microtração, estando dependente do sistema adesivo utilizado.

The idea of using root canals for the retention of restorations of endodontically treated teeth is not new. The post function is to provide retention and support for the restoration material. The present work assessed the adhesive resistance of one dual adhesive system (Excite DSC), one chemical adhesive system (Alloybond), one dual resin cement (Variolink II) and one chemical resin cement (C&B Cement) in fiberglass post cementation (Reforpost). Forty sound human canines, extracted due to periodontal problems, were used. The anatomic crowns of the teeth were cut at the cementoenamel junction. Fiberglass posts Reforpost (Angelus) were cemented, and 4 groups were formed with 10 samples each. The samples were stored in distilled water at 37ºC for 24 hours. After this period, the teeth were fixed in stainless steel tubes with self-curing acrylic resin using a parallelometer. Subsequently, a same size new tube was positioned upside down on the first one in order to hold the fiberglass post up after its setting. A guide tube with positioning posts at both ends was used to standardize all the samples. The samples were positioned in an universal testing machine (Instron) for the traction tests. The comparison of the adhesive systems showed that Alloybond presented higher adhesive resistances, regardless of the resin cement used. There was no statistically significant difference between the resin cements Variolink II and C&B Cement.
A idéia de se usar os condutos radiculares como forma de retenção de restaurações de dentes tratados endodonticamente não é nova. A função do pino é oferecer retenção e suporte para o material restaurador. O presente trabalho avaliou a resistência adesiva de um sistema adesivo dual (Excite DSC), um sistema adesivo químico (Alloybond), um cimento resinoso dual (Variolink II) e um cimento resinoso químico (C&B Cement) na cimentação de pinos de fibras de vidro (Reforpost). Foram utilizados quarenta caninos humanos hígidos, extraídos por indicação periodontal. Os dentes tiveram suas coroas anatômicas seccionadas na junção amelocementária. Pinos de fibras de vidro Reforpost (Angelus) foram cimentados, sendo formados 4 grupos com 10 corpos-de-prova cada. As amostras foram armazenadas em água destilada a 37ºC por 24 horas. Após este período os dentes foram fixados em tubos de aço inoxidável com resina acrílica auto-polimerizável, com o auxílio de um paralelômetro. A seguir um novo tubo de dimensões iguais foi posicionado sobre o primeiro, e vertido sobre este resina acrílica para reter o pino de fibras de vidro após sua presa. Um tubo guia com pinos posicionadores em suas extremidades foi utilizado para padronizar todos os corpos-de-prova. Os corpos-de-prova foram posicionados em uma máquina de ensaios universais (Instron) onde se realizaram testes de tração dos mesmos. Na comparação entre os sistemas adesivos, o Alloybond apresentou maiores resistências adesivas, independente do cimento resinoso utilizado. Os cimentos resinosos Variolink II e C&B Cement não apresentaram diferença estatisticamente significante entre si.

Made available in DSpace on 2017-07-24T19:22:14Z (GMT). No. of bitstreams: 1 Jose David.pdf: 1396926 bytes, checksum: 7d3efdcd4df11b4c6bee44febd2ff0bb (MD5) Previous issue date: 2005-11-18
The purpose of this study was to evaluate “in vitro” the bond strength of the self etch adhesive systems One Coat SE Bond, Self Etch Bond, and XENO®III with the dentin substrate, by means of the microtensile bond strength test, after dentin deproteinization. The conventional adhesive system Adper Single Bond™/3M™-ESPE™ was used as group control. Thirty five human integral third molars were chosen. Theirs occlusal surfaces were cut 3mm±1mm. The dentin surfaces polished with silicon carbide sandpaper of granulation 600 during 1min, in a Politriz. Each group (n=5) received its respective adhesive systems, GI: controle (hybrid layer); GII, GIV and GVI: self etch adhesive systems (reaction-integration); GIII, GV and GVII: self etch adhesive systems (deproteinization). The teeth were restored with resin composite Filtek Z-250 3M™/ESPE™. 24 hours after, the teeth were sectioned using a diamond saw mounted in a Labcut 1010 machine, to get perpendicular sections to the bonding interface with a cross-sectional area to the approximately 0,7 mm2. Were selected 3 specimens per group. Which were prepared and analyzed through the scanning electronic microscope of camp emission and the “confocal laser scanning microscope”, the remaining specimens were submitted to microtensile bond strength in an universal testing machine, at a crosshead speed of 1 mm/min. the mode of fracture was observed using a optic microscope. For each one of the self etching adhesive systems a viscosity test was accomplished. The values of bond strength were submitted to statistical analysis using the Kruskal-Wallis test. The results had shown that the self etch adhesive system XENO®III, after the deproteinization with NaOCl 5,2% (43,60±11,44 MPa) presented the higher values of bond strength. The lowest values were observed in the self etch adhesive system One Coat SE Bond with and without deproteinization (27,50±8,75 MPa) and (27,07±7,27 MPa) respectively. The Self Etch Bond with NaOCl 5,2% demonstrated higher values of bond strength. The microscopy analyses allowed to observed the differences between the adhesive interfaces gotten (hybrid layer, reaction-integration, deproteinization). By this study was possible demonstrated that the dentin deproteinization through the application of NaOCl 5,2%, not influenced on the bond strength of the self etch adhesive systems One Coat SE Bond and XENO®III. In the self etch adhesive system Self Etch Bond with NaOCl the bond strength increased significantly.
O objetivo deste trabalho foi avaliar “in vitro” a resistência adesiva dos sistemas adesivos autocondicionantes One Coat SE Bond, Self Etch Bond, e o XENO®III com o substrato dentinário, por meio do teste de microtração, após a desproteinização dentinária. O sistema adesivo convencional Adper Single Bond™/3M™-ESPE™ foi utilizado como grupo controle. Foram selecionados 35 terceiros molares humanos íntegros. As superfícies oclusais foram cortadas 3mm±1mm. As superfícies de dentina polidas com lixas de carbureto de silício de granulação 600 por 1 min., numa Politriz. Cada grupo (n=5) recebeu os respectivos sistemas adesivos GI: controle (camada híbrida); GII, GIV e GVI: sistemas adesivos autocondicionantes (reação-integração); GIII, GV e GVII: sistemas adesivos autocondicionantes (desproteinização). Os dentes foram restaurados com resina composta Filtek Z-250 3M™/ESPE™. 24 horas após, os dentes foram seccionados usando um disco de diamante montado numa máquina LABCUT 1010, e obter seções perpendiculares da interface adesiva, com uma área de seção transversal de aproximadamente 0,7 mm2 . Foram selecionados 3 espécimes por grupo, os quais foram preparados e analisados em microscópio eletrônico de varredura de emissão de campo e “confocal laser scanning microscope”, os espécimes restantes foram submetidos ao teste de microtração, numa máquina de ensaios universal, a uma velocidade de 1 mm/min. Os modos de fratura foram visualizados utilizando um microscópio óptico. Para cada um dos sistemas adesivos autocondicionantes foi realizado um teste de viscosidade. Os valores de resistência foram submetidos ao teste estatístico de Kruskal-Wallis. Os resultados mostraram que o sistema adesivo autocondicionantes XENO®III após a desproteinização com NaOCl 5,2% (43,60±11,44 MPa), apresentou os maiores valores de resistência adesiva. Os menores valores foram observados no sistema adesivo autocondicionante One Coat SE Bond com e sem desproteinização (27,50±8,75 MPa) e (27,07±7,27 MPa) respectivamente. O Self Etch Bond com NaOCl 5,2%, apresentou maiores valores de resistência adesiva. A análise de microscopia permitiu observar as diferenças entre as interfaces adesivas obtidas (camada híbrida, reação-integração, e desproteinização). Para este estudo foi possível demonstrar que, a desproteinização dentinária por meio da aplicação de NaOCl 5,2% por 40 seg., não influenciou na resistência adesiva, dos adesivos autocondicionantes One Coat SE Bond e do XENO®III. No adesivo autocondicionante Self Etch Bond com NaOCl, a resistência adesiva aumentou significativamente. Palavras-Chave: Sistemas Adesivos; Hipoclorito de sódio; Resistência Adesiva à Tração.

Investigou-se a influência da inclinação das paredes de dentina (paralela ou perpendicular à ação da gravidade) e da variação regional dos espécimes (terços cervical ou oclusal) na resistência adesiva e na espessura da camada de adesivo. Vinte e cinco molares humanos foram seccionados no sentido mésio-distal e paralelamente ao seu longo eixo, obtendo-se secções vestibulares e linguais, as quais foram lixadas produzindo-se superfícies planas de dentina. Sistemas adesivos (Adper Single Bond-SB e Prime & Bond 2.1- PB2.1) foram aplicados na dentina, ora paralelamente ora perpendicularmente à ação da gravidade, padronizando-se o volume de adesivo (3,5 µl por gota) através do uso de uma micropipeta e seguindo-se as instruções dos fabricantes. Os grupos de estudo foram: 1A (SB, paralelo), 1B (SB, perpendicular), 2A (PB2.1, paralelo) e 2B (PB2.1, perpendicular). Após 24h de armazenamento em água deionizada a 37°C, espécimes foram preparados na forma de palitos de dentina com área adesiva de 0,8 mm2, aproximadamente. Na seqüência, foi determinada a espessura do adesivo de cada espécime, em micrômetros (µm), sob microscopia óptica (200X de aumento) e auxílio do programa Image Pro-Plus 4.5. Posteriormente, os espécimes foram submetidos à microtração sob velocidade de 0,5 mm/min. Todos os espécimes fraturados foram examinados sob microscopia óptica (40X de aumento) para a determinação dos planos de fratura. Os dados coletados foram submetidos aos testes ANOVA a 1 e 2 critérios e SNK (? = 0,05). Para determinação da correlação entre resistência adesiva e espessura do adesivo foi utilizado o teste de Correlação de Pearson. Os valores médios (MPa±d.p.) de resistência adesiva dos grupos 2A (52,93±15,19) e 2B (52,27±16,54) foram superiores àqueles dos grupos 1A (39,09±12,90) e 1B (32,94±12,42), independente da inclinação das paredes de dentina dos mesmos. Não houve diferença nos valores de resistência adesiva à dentina, independente da variação regional do espécime. Os valores médios (µm±d.p.) de espessura da camada de adesivo dos grupos 1A (11,24±2,92) e 1B (18,11±7,31) foram superiores àqueles dos grupos 2A (4,20±1,81) e 2B (3,87±1,29) (p > 0,05). O grupo 1B promoveu os maiores valores de espessura de adesivo, seguido do grupo 1A. As espessuras do adesivo nos grupos 2A e 2B apresentaram-se similares entre si. Houve influência da variação regional do espécime na espessura de adesivo somente para o grupo 1B. Não houve correlação entre resistência adesiva e espessura de adesivos para ambos SB e PB2.1 (r = -0,224, p = 0,112 e r = 0,099, p = 0,491, respectivamente). Conclui-se que a influência da inclinação das paredes de dentina e da variação regional dos espécimes na espessura da camada de adesivo é material-dependente, porém não influem na resistência adesiva dos sistemas adesivos à dentina.
To determine the effect of the inclination of dentin surfaces (parallel or perpendicular to the force of gravity) and the regional variation of specimens (cervical or occlusal thirds) on the dentin bond strength and adhesive layer thickness. Twenty-five extracted human molars were sectioned in a mesio-distal direction to expose flat dentin. Standardized drop volumes of adhesive systems (Single Bond-SB and Prime & Bond 2.1-PB2.1) were applied to dentin according to manufacturers instructions. Teeth were randomly divided into the following groups: 1A (SB, parallel), 1B (SB, perpendicular), 2A (PB2.1, parallel) and 2B (PB2.1, perpendicular). Teeth were stored in 37°C distilled water for 24h and then serially sectioned to obtain sticks with cross-sectional area of approximately 0.8 mm2 for microtensile bond strength test (MTBS). The thickness of adhesive layer of the MTBS specimen was determined in a light microscope at 200X magnification. Forty-eight hours after adhesion procedures the specimens were subjected to MTBS at a crosshead speed of 0.5 mm/min. After testing, the fracture modes of each specimen were determined by examination under a 40X magnification. One and two-way ANOVA and Student- Newman-Keuls-SNK tests were performed do determine differences in MTBS and in adhesive layer thickness among groups. The correlation between MTBS and adhesive layer thickness was compared with Pearson Product Moment Correlation ('alfa' = 0.05). Mean values (MPa±s.d.) for bond strength were higher for groups 2A (52.93±15.19) and 2B (52.27±16.54) than for groups 1A (39.09±12.90) and 1B (32.94±12.42), regardless of the position of dentin surfaces. There was no difference in MTBS, despite the regional variation of specimens. The thickness of adhesive systems (µm±s.d.) was higher for groups 1A (11.24±2.92) and 1B (18.11±7.31) than those for groups 2A (4.20±1.81) and 2B (3.87±1.29). Group 1B provided the greater mean values of adhesive thickness followed by the Group 1A. Similar adhesive thicknesses were found for Groups 2A and 2B, but significantly lower than the other groups. There was a significant influence of the regional variation of specimens on the adhesive thickness of group 1B. No correlation was found between bond strength and adhesive layer thickness for both SB and PB 2.1 (r = -0.224, p = 0.112 and r = 0.099, p = 0.491, respectively). The inclination of dentin surface and the regional variation of specimens on the adhesive layer thickness are materialdependent. These variables do not influence the adhesive systems bond strength to dentin.

Com os sistemas adesivos autocondicionantes, o uso prévio do ácido fosfórico passou a ser dispensado em dentina. Assim, outras soluções foram propostas a fim de se promover uma limpeza da cavidade e otimizar um melhor embricamento do adesivo ao substrato. O objetivo deste estudo foi avaliar a influência de soluções químicas à adesão à dentina bovina, por meio da resistência ao microcisalhamento, de três sistemas adesivos autocondicionantes em função do tempo. Duzentos e quarenta incisivos bovinos foram incluídos, desgastados e polidos em série com lixas de carbeto de silício, obtendo uma superfície planificada de dentina de 10 mm de diâmetro. Os espécimes foram divididos aleatoriamente em 4 grupos, de acordo com a solução aplicada: SF- aplicação de soro fisiológico com 0,9% NaCl (grupo controle); HS- desproteinização com hipoclorito de sódio a 5%, por 2 minuto e HSAA- hipoclorito de sódio a 5%, por 2 minuto seguida da aplicação de ácido ascórbico (ascorbato) a 10%, por 1 minuto; CHX- aplicação de solução clorexidina a (2% por 1 minuto). Às superfícies preparadas foram aplicados três sistemas adesivos autocondicionantes, por grupo - Optibond All-in-One (KERR), Filtek P90-System Adhesive (3M-ESPE) e Adper SE (3M-ESPE), todas seguidas da inserção de resina composta (Filtek Z250 ou Filtek P90). Metade dos espécimes de cada grupo foram armazenados por 24 horas e metade por 6 meses. Após esses períodos, os espécimes foram submetidos ao teste de microcisalhamento, em uma máquina de ensaios universal (Emic, na velocidade de 0,5mm/min). Os dados foram avaliados estatisticamente através de análise de variância (ANOVA) a três critérios e testes de comparações múltiplas de Tukey ambos considerando a=0,05. O adesivo Filtek P90-System Adhesive foi o único que manteve a resistência adesiva após o envelhecimento, porém, os dois tratamentos de superfície contendo hipoclorito de sódio influenciaram negativamente. Já com a clorexidina não houve diferença estatisticamente significante comparada ao grupo controle. O adesivo OptiBond All- In-One (Kerr) foi influenciado positivamente pelo hipoclorito de sódio e hipoclorito de sódio mais ascorbato, no tempo de 24 horas. Sendo de iqual resultado com o envelhecimento em solução aquosa. Adper SE (3M-ESPE) sofreu influência dos tratamentos à base de hipoclorito de sódio. O melhor resultado, comparando dois tratamentos com hipoclorito, após o envelhecimento, foi obtido pelo tratamento com o hipoclorito de sódio mais ascorbato sendo estatisticamente idêntico ao grupo controle. Foi concluído que os tratamentos de superficie influenciam na resistência adesiva dos adesivos testados. A clorexidina possibilitou os melhores resultados em quase todos os testes.
With the Self-etching adhesives, acid-etching with phosphoric acid has to be dispensed in dentin. Than, other solutions have been proposed in order to promote the cavity cleaner and improvement in bonding effectiveness. The aim of this study was to investigate the microshear bond strength, with the influence of chemical solutions and time, in three adhesive systems used on bovine dentin. Two hundred and forty bovine incisors were included, and the surface was polished in series with silicon carbide paper, getting flattened dentin surface of 10 mm in diameter. The specimens were randomly divided into four groups, according to the applied solution: SF- saline solution with 0.9% NaCl (control group), HS-deproteinization with sodium hypochlorite at 5%, for 2 minutes and HSAA- sodium hypochlorite 5% for 2 minutes followed by the application of ascorbic acid (ascorbate) and 10% for 1 minute;CHXapplication of chlorhexidine solution (2% for 1 minute). Were applied to surfaces prepared three adhesive systems, per group - Optibond All-in-One (Kerr), Filtek-P90 System Adhesive (3M-ESPE) and Adper SE (3M-ESPE), all followed by the insertion of composite resin ( Filtek Z250 and Filtek P90). Half of the specimens of each group / treatment were stored for 24 hours and half for six months. After these periods were tested using the microshear in a universal testing machine (Emic, the speed of 0.5 mm / min). Results were submitted to three way ANOVA and TUKEY test multiple comparison both considering a = 0.05. The adhesive Filtek P90 System Adhesive was the one who kept the bond strength after aging, however, the two surface treatments containing sodium hypochlorite influenced negatively. With chlorhexidine, there was no statistically significant difference compared to the control group. The adhesive OptiBond All-in-One (Kerr) was affected by the sodium hypochlorite, sodium hypochlorite more ascorbate, at 24 hours. As a result of iqual with aging in aqueous solution. Adper SE (3M-ESPE) was influenced by the treatments using sodium hypochlorite. The best result, comparing two treatments with hypochlorite, after aging, was obtained by treatment with sodium hypochlorite more ascorbate was statistically identical to the control group. It was concluded that the influence of surface treatments on bond strength of adhesives tested. The chlorhexidine resulted in better results in almost every test.

O objetivo deste trabalho foi analisar em Microscopia Ótica (MO), Espectroscopia micro-Raman (µR) e Microscopia Eletrônica de Varredura (MEV), a interface adesiva em dentina proporcionada por três sistemas adesivos aplicados in vivo e in vitro. Na condição in vivo, pacientes com primeiros prémolares superiores hígidos indicados para extração, por razões ortodônticas, foram utilizados. Cavidades classe I com 0,5mm além da junção esmalte-dentina foram realizadas, nos dentes, com broca carbide 245 em alta rotação. Foram, então aplicados três sistemas adesivos diferentes foram aplicados, de acordo com as instruções dos respectivos fabricantes: Single Bond (SB-3M), Clearfil SE Bond (CSEB-Kuraray) e One Up Bond-F (OUB-Tokuyama). Aplicados esses, as cavidades foram restauradas incrementalmente com resina composta TPH Spectrum (Dentsply). Em seguida os dentes foram extraídos e armazenados em solução de timol a 0,1%. In Vitro, os mesmos procedimentos foram realizados em pré-molares extraídos. Após os dentes foram levados à uma máquina de cortes e seccionados, com auxílio de um disco de corte em espécimes contendo a interface, com dimensões 2mmx2mmx6mm de comprimento, sendo 2 espécimes para cada dente. Um dos espécimes foi levado a um micrótomo de tecido duro onde fatias com espessura de 5µm foram obtidas e coradas com Tricromo de Goldner. As fatias foram, então, analisadas em um microscópio óptico com aumento de 100 vezes. Nesta técnica a dentina mineralizada se cora de verde, o colágeno não infiltrado de vermelho e o sistema adesivo de beje translúcido. Após o mesmo espécime foi utilizado para análise em espectroscopia micro-Raman. O espécime adjacente foi desidratado em seqüência ascendente de etanol e analisado em microscopia eletrônica de varredura. Os resultados da MO para o sistema SB mostraram a presença de uma grande área corada de vermelho, indicando colágeno exposto ou não devidamente infiltrado pelo sistema adesivo para ambas as situações porém, in vivo, esta camada se mostrou maior. Para o sistema CSEB esta camada se corou de roxa, consistente ao longo de toda interface, indicando também a presença de colágeno disponível para reação com o corante, para ambas as situações. Para o sistema OUB esta camada também se corou de roxa, porém in vivo esta se mostrou mais fina e irregular que in vitro. Em MEV o sistema SB apresentou uma camada híbrida granular e porosa para ambas as situações. In vitro esta se mostrou mais espessa e regular ao longo da interface ao contrário da condição in vivo. Grandes diferenças foram observadas em relação aos tags de resina, onde in vivo, se apresentaram mais finos e curtos. Para o sistema CSEB a camada híbrida se mostrou mais fina quando comparada ao sistema SB porém, mais homogênea e compacta ao longo da interface para ambas as situações. Grandes diferenças foram observadas em relação aos tags de resina onde in vivo foram significativamente em menor número, curtos e finos. Para o sistema OUB in vitro a camada híbrida se apresentou fina porém, homogênea em sua extensão com a presença de longos tags. In vivo a camada híbrida se apresentou bastante fina e até difícil de se detectar. O tags se apresentaram quase inexistes ou muito dobrados devido à pobre polimerização desse sistema. As análises em µR para o sistema SB mostraram uma maior contribuição do sistema adesivo nos dois primeiros micrometros da interface, ao passo que, no restante da mesma, houve pouca contribuição dos monômeros adesivos na proteção do colágeno. Para o sistema CSEB a interface se mostrou bastante fina (1µm), para ambas as condições, porém com contribuição, no complexo hibridizado, dos componentes adesivos, colágeno e mineral. Para o sistema OUB in vitro, os espectros também indicaram a presença de uma interface fina, em torno de 1µm, mas também com contribuição dos componentes adesivos, colágeno e mineral. In vivo, esta não pôde ser detectada pelo Raman por ser inexistente ou ser mais fina que a resolução do Raman (1 µm). Realizada as análises da interface em ambas condições experimentais, com os diferentes sistemas adesivos utilizados, conclui-se que: a condição in vivo proporcionou uma interface de menor qualidade para todos os sistemas. O sistema CSEB aparentemente proporcionou uma melhor qualidade de interface e o sistema OUB a pior. O uso dessas três técnicas integradas permitiu uma análise completa, qualitativa e quantitativa da interface adesiva produzida por esses três sistemas, em ambas as condições testadas.
The aim of this research was to analyze in Light Microscopy (LM), micro-Raman Spectroscopy (µR) and Scanning Electron Microscopy (SEM), the dentin-adhesive interface produced by three different bonding systems applied in vivo and in vitro. In in vivo condition patients with the first upper premolars, to be extract for orthodontic reasons, were used. Class I cavities with 0.5mm below the dentin-enamel junction were performed, with carbide bur in high speed. Following, three different bonding systems were applied in accordance with their manufacturer instruction: Single Bond (SB-3M), Clearfil SE Bond (CSEB-KURARAY) and One Up Bond-F (OUBTokuyama), and the cavities restored, incrementally, with composite resin TPH Spectrum (Dentsply). After restoration the teeth were extracted and stored in 0,1% tymol solution. In vitro, the same procedures were performed in extracted upper premolars. Following, the teeth were taken to a cutting machine and cross-sectioned with as diamond saw in specimens with 2mmX2mmx6mm dimensions, being 2 specimens for each tooth. One of the specimen was taken to a hard tissue microtome were 5µm slabs were obtained and stained with Goldner´s Tricrome. The slabs were analyzed in a Light Microscope with 100 times magnification. In this technique, the mineralized dentin is stained green, the collagen is stained red and the bonding system a pale orange. After, the same specimen was used for micro-Raman analysis. The adjacent specimen was dehydrated in ascendant ethanol sequence and analyzed in scanning electron microscopy. The LM results for SB showed the presence of a large area stained red for both conditions, indicating the presence of exposed or non protected collagen by the bonding system. This area was larger in vivo than in vitro. For CSEB this layer war purple stained and consistent along the interface for both situations, indicating, also, collagen available to react with the staining. For OUB this layer was also purple however, in vivo, this layer was thinner and inconsistent than in vitro. In SEM analysis, SB bonding system presented a porous hybrid layer for both situations. In vitro this layer was thicker and regular along the interface and, in vivo, thinner and irregular. Big differences were observed related to the resin tags. In vivo they were thinner and shorter. For CSEB the hybrid layer was thinner when compared with SB however, more homogeneous and compact along the interface for both situations. Big differences were observed related to the resin tags. In vivo, they were significantly in fewer amounts, shorter and thinner. For OUB in vitro, the hybrid layer was thin, however, homogeneous and with long tags. In vivo, the hybrid layer was very thin, almost undetectable. The resin tags were almost non-existent or bended due to poor polymerization of this system. In micro-Raman analysis for SB showed a greater contribution of the bonding system in the first two micrometers of the interface was detected and, in the rest of the interface, there was few contribution of the resin monomers in the collagen protection. For CSEB the interface was thin (1µm), for both conditions, however, with contribution, in the hybridized complex, of the adhesives components, collagen and mineral. For OUB in vitro, the spectras also indicated the presence of a thin interface, among 1µm, but also, with contribution of the bonding components, collagen and mineral. In vivo, the interface could not be detected by the Raman, for being inexistent, or by the fact to be thinner than the Raman resolution (1µm). After all these analysis of the bonding interface, for both conditions, and with these different bonding systems, it can be concluded that: in vivo condition produced a less-quality interface for all the system. CSEB apparently produced a better-quality interface and OUB the worst. The use of these three techniques together allowed a complete analysis, qualitative and quantitative, of the dentin-bonding interface produced by these three bonding systems, for both situations.

Made available in DSpace on 2017-07-24T19:22:05Z (GMT). No. of bitstreams: 1 FELIPE GUTIERREZ REYES.pdf: 2973646 bytes, checksum: 0e8c702449c97c861e9f0314e3b69e2f (MD5) Previous issue date: 2016-02-23
Objectives: This study evaluated the effect of addition of copper nanoparticles at different concentrations into a simplified etch-and-rinse (ER) adhesive system (Ambar [AM]) on antimicrobial activity (AMA), degree of conversion of adhesives discs (DC-d) and dentin-resin interface (DC-i), the ultimate tensile strength (UTS), 28-day cumulative water sorption (WS), solubility (So) and copper release (CR) as well as immediate (IM) and 1-year (1Y) resin–dentine bond strength (μTBS) and nanoleakage (NL). Methods: Seven experimental adhesive systems were formulated according to the addition of copper nanoparticles (0 [control], 0.0075, 0.015, 0.06, 0.1, 0.5 and 1%) in AM adhesive system. We tested the antimicrobial activity of synthesized adhesives against Streptococcus mutans using agar diffusion assays. For DC-d, specimens were constructed and tested after 24 h for FTIR and micro-Raman spectroscopy. For UTS, specimens were tested after 24 h and 28 days. For WS and So, after specimens build-up, they were stored in water and the properties measured for 28 days. For CR, specimens were stored in 2% nitric acid solution and the properties were measured for 28 days. The occlusal enamel of thirty-five molars was removed and adhesives were applied to dentine surface after 37% phosphoric acid etching. After composite resin build-ups, specimens were longitudinally sectioned to obtain resin–dentine bonded sticks (0.8 mm2). Specimens were tested in tension at 0.5 mm/min in IM or 1Y (μTBS). For NL, 2 bonded sticks from each tooth were prepared and analyzed under SEM in IM or 1Y. For DC-i, 2 bonded sticks were prepared and analyzed under micro-Raman spectroscopy. The μTBS and NL data of each adhesive were subjected to two-way repeated measures ANOVA. For UTS, WS, So, copper release, DC-d and DC-i data of each adhesive were subjected to a one-way ANOVA. Tukey’s post hoc test was used for pair-wise comparisons (α = 0.05). Results: The addition of copper nanoparticles provided antimicrobial properties to the adhesives at all concentrations (p < 0,05), and did not influence UTS, WS and SO (p > 0.05). Higher CR was observed in adhesives with higher concentration of copper nanoparticles (p < 0.05). The addition of 1% of copper nanoparticles decreased the DC-d and DC-i significantly. After 1Y, significant reductions of μTBS and increases of NL were observed in the control group (p < 0.05). Reductions of μTBS and increase of NL over time were not observed for copper-containing adhesives.Conclusions: The addition of copper nanoparticles in concentrations up to 0.5% in the simplified ER Ambar adhesive system may be an alternative to provide antimicrobial properties, increase the long-term stability of resin–dentine interfaces, 12 without reducing adhesives’ mechanical properties evaluated.
Objetivos: Este estudo avaliou o efeito da adição de nanopartículas de cobre, em diferentes concentrações, em um sistema adesivo convencional (CON) simplificado Ambar [FGM] sobre a atividade antimicrobiana (AAM), grau de conversão de corpos de prova de adesivos (GC-c) e na interface de união a dentina (GC-i), resistência máxima à tração (RT), sorção cumulativa de água (SO), solubilidade (SB) e liberação de cobre (LC) durante 28 dias, bem como a resistência de união (RU) e nanoinfiltração (NI) na interface de união à dentina nos tempos imediatos (IM) e após 1 ano (1A). Material e métodos: Sete sistemas adesivos experimentais foram formulados de acordo com a adição de nanopartículas de cobre (0 [controle], 0,0075, 0,015, 0,06, 0,1, 0,5 e 1%) no sistema adesivo Ambar. Foi testada a atividade antimicrobiana dos adesivos formulados contra Streptococcus mutans por meio de ensaios de difusão em ágar. Para GC-c, as amostras foram construídas e testadas após 24 h por meio de espectrofotometria no infravermelho com Transformação de Fourier (FTIR) e espectroscopia de micro-Raman. Para RT, as amostras foram testadas depois de 24 horas e 28 dias. Para SO e SB, depois de confeccionados os espécimes, eles foram armazenados em água e as propriedades medidas por 28 dias. Para LC, as amostras foram armazenadas em solução de ácido nítrico a 2% e as propriedades medidas durante 28 dias. O esmalte oclusal de trinta e cinco molares foi removido e os adesivos foram aplicados na superfície da dentina depois de condicionamento com ácido fosfórico a 37%. Depois de restaurações de resina composta, os espécimes foram seccionados longitudinalmente para se obter espécimes (palitos) de resina-dentina (0,8 mm2). Os espécimes foram testados em tensão a 0,5 mm/min no IM ou 1A (RU). Para NI, 2 espécimes de cada dente foram preparadas e analisadas em MEV e testados no IM ou 1A. Para GC-i, 2 espécimes foram preparados e analisados sob espectroscopia de micro-Raman. Os dados do RT foram analisados por uma análise de variância de 2 fatores. Para AAM, SO, SB, e liberação de cobre, os dados foram analisados por análise de variância de fator único, e para RU e NI os dados foram submetidos a análise de variância de 2 fatores para medidas repetidas. Também foi feito o teste post hoc de Tukey para múltiplas comparações. A significância estatística foi predefinida em α = 0,05.Resultados: A adição de nanopartículas de cobre adicionou propriedades antimicrobianas aos adesivos em todas as concentrações (p < 0,05), e não influenciou a RT, SO e SB (p > 0,05). LC elevadas foram observadas em adesivos com maior concentração de nanopartículas de cobre (p < 0,05). A adição de 1% de 10 nanopartículas de cobre diminuiu significativamente o GC-c e GC-i. Após 1 ano, decréscimos significativos de RU e aumentos de NI foram observados no grupo controle (p < 0,05). Decréscimos significativos de RU e aumentos de NI não foram observados nos adesivos contendo cobre (p > 0,05). Conclusões: A adição de nanopartículas de cobre em concentrações de até 0,5% no sistema adesivo convencional simplificado Ambar pode ser uma alternativa para adicionar atividade antimicrobiana e aumentar a estabilidade a longo prazo das interfaces resina-dentina, sem comprometer as propriedades mecânicas dos adesivos.

Made available in DSpace on 2014-06-11T19:31:27Z (GMT). No. of bitstreams: 0 Previous issue date: 2003-11-10Bitstream added on 2014-06-13T20:41:47Z : No. of bitstreams: 1 mazur_rf_dr_arafo.pdf: 2691655 bytes, checksum: aa6766566238765dc0a1f4d5cb633eda (MD5)
O objetivo deste trabalho foi realizar, in vitro, avaliação da resistência de adesiva pelo teste de microtração de dez sistemas adesivos diferentes. Os sistemas adesivos One Up Bond F - Tokuyama, Clearfil SE Bond - Kuraray, Adper Prompt L-Pop, Single Bond - 3M/ESPE, One Step - Bisco, One Step Plus - Bisco, Prime&Bond NT - Dentsply, Excite - Vivadent, Scotchbond Multi - Uso - 3M/ESPE e All Bond 2 - Bisco. Para a realização do teste foram utilizados quarenta dentes molares hígidos, sendo que destes dentes dez foram utilizados para a microscopia eletrônica de varredura. Para a realização do teste de microtração os dentes foram cortados na superfície oclusal com disco diamantado e posteriormente foram desgastados com discos de lixa. Posteriormente as amostras foram restauradas com os respectivos sistemas adesivos e resina composta Z-100 com tempo de polimerização de 40 segundos cada incremento. Após vinte e quatro horas de armazenagem em temperatura de 37ºC os dentes foram seccionados com disco diamantado com finalidade de obter palitos com área de 1,0 +- 0,2 mm2. Após o corte os palitos foram armazenados em temperatura de 37ºC por vinte e quatro horas e em seguida foram levados para a máquina de ensaio universal EMIC 500 DL onde os palitos foram tracionados com velocidade de 1 mm/min. Os resultados foram analisados pelo através dos testes de normalidade de Lilliefors e de homogeneidade de variância de Bartlett. Quando alguns dos pressupostos não se verificaram, utilizou-se o teste não paramétrico de Kruskal - Wallis. Os resultados obtidos foram em ordem decrescente de 36,73 +- 10,52 para o sistema adesivo One Up Bond F, seguido do sistema de três etapas All Bond 2 com 34,29 +- 12,63 para o sistema adesivo One Step Plus foi de 33,18 +- 11,33 para o sistema Adper Prompt L-Pop de 31,76 +- 11,3, sistema One Step de 29,02 +- 11,28, para o... .
The aim of this study was to analyze the bond strength of ten adhesive systems: One Up Bond F - Tokuyama (OU); Adper Prompt L-Pop - 3M-ESPE (AP); Clearfil SE Bond - Kuraray CO. (SE); Prime Bond NT - Caulk-Dentsply (NT); Single Bond - 3M-ESPE (SB); One Step - Bisco (OS); One Step Plus - Bisco (OP); Excite - Vivadent (EX); Scotchbond Multi - Purpose (SMP) e All Bond 2 - Bisco (AB). Methods: Forty freshly extracted human teeth were transversely wetcut using a diamond disk in order to expose the occlusal dentin surface. Then the adhesive systems were applied according to the manufacturer's instruction. The teeth were restored with composite resin Z-100 (3M) and stored in distilled water at 37ºC for 24 hours. A slow-speed diamond disk was used to prepare microtensile test specimens, with a bonded area of 1,00 +- 0,2 mm2. Each group was composed of thirty sticks, which were stored in distilled water at 37ºC for 24 hours. The sticks were bonded on a universal testing machine at a cross head speed of 1 mm/min. The following results demonstrate values microtensile bond strengths in MPa. Data were statistically analyzed by Kruskal-Wallis Test (p<-0.05). The bond strength values were 36,73 +- 10,52 for One Up Bond F, 34,29 +- 12,63 for All Bond 2, 33,18 +- 11,33 for One Step Plus, 31,76 +- 11,3 for Adper Prompt L-Pop, 29,02 +- 11,28 for One Step, 28,82 +- 14,74 for Single Bond, 28,08 +- 12,09 for Clearfil SE Bond, 26,31 +- 9,02 for Scotchbond Multi - Purpose, 21,35 +- 10,22 for Prime&Bond NT and 19,52 +- 10,08 for Excite. Ten teeth were analysed by SEM and all of them showed resin into the dentin tubules. Most of fractures were adhesive in the composite/teeth interface. One up bond F (OU) resulted in higher bond strength when compared to all the other systems tested and Excite resulted in lower bond strength. Self-etching systems were not statistically... (Complete abstract, click electronic address below).

O propósito do presente estudo foi analisar o efeito da aplicação de múltiplas camadas consecutivas de dois sistemas adesivos convencionais de dois passos na difusão resinosa e padrão de distribuição dos componentes monoméricos resinosos. Dezesseis terceiros molares humanos hígidos foram tratados com os sistemas adesivos convencionais de dois passos de acordo com as instruções dos fabricantes ou com aplicações em múltiplas camadas consecutivas. Os espécimes foram seccionados paralelamente aos túbulos dentinários e as superfícies submetidas ao polimento com lixas 600, 1200, 1800, 2000 e 4000. Os espectros Raman foram coletados ao longo de uma linha perpendicular a interface adesivo-resina em intervalos de 1 ou 2 m. As medidas de difusão da resina adesiva e distribuição dos componentes monomériccos foram avaliadas pelos picos Raman de 1113 cm-1, 1609 cm-1 e 1454 cm-1. O gradiente de desmineralização usado na determinação da região de hibridização foi avaliado pelo pico de 960 cm-1 da apatita. De acordo com os resultados obtidos, a aplicação de múltiplas camadas apresentou uma tendência de homogeneização dos componentes poliméricos, dependente da composição química da resina adesiva.
The present study analyzed the effect of multiple consecutive adhesive coatings on the pattern of resin diffusion and distribution of monomer components through demineralised dentin after application of two total-etch adhesives. Resin bonded dentin specimens were prepared using two total-etch adhesives (Prime&Bond NT2.1 and Adper Single Bond). The specimens were sectioned parallel to dentinal tubules and the surfaces were polished using 600, 1200, 1800, 2000 and 4000 silicon-carbide papers. Raman spectra were recorded along a line perpendicular to the dentin-resin interface in steps of 1 or 2 m. The measurements of resin diffusion and distribution of monomer components were made on a relative basis by comparing the bands 1113, 1609 and 1454 cm-1. The gradient of dentin demineralization, designed to 960 cm-1, was used to determine the extent of hybridization. From the results of the present study the application of multiple coatings of adhesive showed a trend to produce a homogeneous hybrid layer.

Orientador: José Roberto Cury Saad
Banca: Marcelo Ferrarezi de Andrade
Banca: Welingtom Dinelli
Banca: Rodrigo Nunes Rached
Banca: Paulo Sérgio Quagliatto
Resumo: O objetivo deste trabalho foi realizar, in vitro, avaliação da resistência de adesiva pelo teste de microtração de dez sistemas adesivos diferentes. Os sistemas adesivos One Up Bond F - Tokuyama, Clearfil SE Bond - Kuraray, Adper Prompt L-Pop, Single Bond - 3M/ESPE, One Step - Bisco, One Step Plus - Bisco, Prime&Bond NT - Dentsply, Excite - Vivadent, Scotchbond Multi - Uso - 3M/ESPE e All Bond 2 - Bisco. Para a realização do teste foram utilizados quarenta dentes molares hígidos, sendo que destes dentes dez foram utilizados para a microscopia eletrônica de varredura. Para a realização do teste de microtração os dentes foram cortados na superfície oclusal com disco diamantado e posteriormente foram desgastados com discos de lixa. Posteriormente as amostras foram restauradas com os respectivos sistemas adesivos e resina composta Z-100 com tempo de polimerização de 40 segundos cada incremento. Após vinte e quatro horas de armazenagem em temperatura de 37ºC os dentes foram seccionados com disco diamantado com finalidade de obter palitos com área de 1,0 +- 0,2 mm2. Após o corte os palitos foram armazenados em temperatura de 37ºC por vinte e quatro horas e em seguida foram levados para a máquina de ensaio universal EMIC 500 DL onde os palitos foram tracionados com velocidade de 1 mm/min. Os resultados foram analisados pelo através dos testes de normalidade de Lilliefors e de homogeneidade de variância de Bartlett. Quando alguns dos pressupostos não se verificaram, utilizou-se o teste não paramétrico de Kruskal - Wallis. Os resultados obtidos foram em ordem decrescente de 36,73 +- 10,52 para o sistema adesivo One Up Bond F, seguido do sistema de três etapas All Bond 2 com 34,29 +- 12,63 para o sistema adesivo One Step Plus foi de 33,18 +- 11,33 para o sistema Adper Prompt L-Pop de 31,76 +- 11,3, sistema One Step de 29,02 +- 11,28, para o... (Resumo completo, clicar acesso eletrônico abaixo).
Abstract: The aim of this study was to analyze the bond strength of ten adhesive systems: One Up Bond F - Tokuyama (OU); Adper Prompt L-Pop - 3M-ESPE (AP); Clearfil SE Bond - Kuraray CO. (SE); Prime Bond NT - Caulk-Dentsply (NT); Single Bond - 3M-ESPE (SB); One Step - Bisco (OS); One Step Plus - Bisco (OP); Excite - Vivadent (EX); Scotchbond Multi - Purpose (SMP) e All Bond 2 - Bisco (AB). Methods: Forty freshly extracted human teeth were transversely wetcut using a diamond disk in order to expose the occlusal dentin surface. Then the adhesive systems were applied according to the manufacturer's instruction. The teeth were restored with composite resin Z-100 (3M) and stored in distilled water at 37ºC for 24 hours. A slow-speed diamond disk was used to prepare microtensile test specimens, with a bonded area of 1,00 +- 0,2 mm2. Each group was composed of thirty sticks, which were stored in distilled water at 37ºC for 24 hours. The sticks were bonded on a universal testing machine at a cross head speed of 1 mm/min. The following results demonstrate values microtensile bond strengths in MPa. Data were statistically analyzed by Kruskal-Wallis Test (p<-0.05). The bond strength values were 36,73 +- 10,52 for One Up Bond F, 34,29 +- 12,63 for All Bond 2, 33,18 +- 11,33 for One Step Plus, 31,76 +- 11,3 for Adper Prompt L-Pop, 29,02 +- 11,28 for One Step, 28,82 +- 14,74 for Single Bond, 28,08 +- 12,09 for Clearfil SE Bond, 26,31 +- 9,02 for Scotchbond Multi - Purpose, 21,35 +- 10,22 for Prime&Bond NT and 19,52 +- 10,08 for Excite. Ten teeth were analysed by SEM and all of them showed resin into the dentin tubules. Most of fractures were adhesive in the composite/teeth interface. One up bond F (OU) resulted in higher bond strength when compared to all the other systems tested and Excite resulted in lower bond strength. Self-etching systems were not statistically... (Complete abstract, click electronic address below).
Doutor

O objetivo da presente tese foi desenvolver um adesivo com nanocápsulas (NCs), contendo indometacina, e um sistema adesivo com nanocápsulas (NC), contendo indometacina e triclosan, e avaliar suas propriedades. As NCs foram produzidas por meio do método de deposição de polímero, secas e caracterizadas quanto ao tamanho de partículas, à forma, quantidade de fármaco encapsulado e citotoxicidade. Uma resina adesiva foi formulada. Foram adicionadas ao adesivo 1%, 2%, 5% e 10% de NCs em massa, e um grupo permaneceu sem NC. As NCs, contendo indometacina e triclosan, foram também incorporadas no primer comercial a 2% em peso e um grupo permaneceu sem NCs. Os adesivos foram avaliados quanto ao GC imediato e tardio, à degradação em solvente, liberação dos fármacos, difusão de indometacina pela dentina e resistência de união. O adesivo com 10% de NCs, contendo indometacina, foi também avaliado quanto à ação anti-inflamatória em modelo animal. O primer e o adesivo com as diferentes concentrações de NCs, contendo indometacina e triclosan, foram avaliados quanto à liberação dos fármacos, difusão de indometacina pela dentina, ao efeito antimicrobiano, grau de conversão (GC) in situ, ângulo de contato e à resistência de união à microtração. Os dados foram analisados por ANOVA, Tukey e teste t. As NCs apresentaram forma esférica e viabilidade celular acima de 80%. As NCs, contendo indometacina, apresentaram diâmetro médio de 165 nm e as NCs, contendo indometacina e triclosan, 159 nm. O adesivo, contendo 10% de NCs com indometacina, apresentou efeito anti-inflamatório. A incorporação de NCs não alterou o GC, que variou de 63,63 ± 1,01% a 70,50 ± 2,08%. A degradação em solvente não foi alterada com 2% de NCs. Tanto os adesivos quanto o primer apresentaram liberação controlada. A indometacina permeou através da dentina. O adesivo e primer também apresentaram efeito antimicrobiano. A incorporação de NCs no primer e no adesivo não influenciou o GC in situ nem a resistência de união imediata, em comparação aos materiais sem NCs. O uso concomitante do primer e adesivo com NCs aumentou o ângulo de contato e diminuiu a resistência de união longitudinal. Conclui-se que o uso do adesivo com a incorporação de NCs tem potencial para proporcionar ações terapêuticas à adesão dentinária.
The aim of the present thesis was to develop an adhesive with nanocapsules (NCs) containing indomethacin and an adhesive system with nanocapsules containing indomethacin and triclosan and to evaluate their properties. NCs were prepared by the interfacial deposition of preformed polymer technique, dried and characterized regarding particle size, encapsulated drug content and cytotoxicity. Adhesive resin was produced. Concentrations of 1%, 2%, 5% and 10% of NCs were added in the adhesive and a group was maintained with no NCs. Indomethacin and triclosan-loaded NCs were also incorporated into a commercial primer in a concentration of 2% and a group was maintained with no NCs. Adhesives were evaluated regarding immediate and late degree of conversion (DC), degradation in solvent, drug release, indomethacin diffusion through dentin and bond strength. The adhesive with 10% of NCs containing indomethacin was also evaluated regarding the anti-inflammatory effect in an animal model. Primer and adhesive with different concentrations of NCs containing indomethacin and triclosan were evaluated regarding drug release, indomethacin diffusion through dentin, antimicrobial effect, in situ degree of conversion, contact angle and bond strength. Data were analyzed through ANOVA, Tukey post-hoc and t-test.NCs presented a spherical shape and cell viability higher than 80%. NCs containing indomethacin presented an averaged size of 165 nm and NCs containing indomethacin and triclosan, 159 nm. The adhesive with 10% of NCs containing indomethacin presented anti-inflammatory effect. The incorporation of NCs presented no alteration of DC, varying from 63.63 ± 1.01% a 70.50 ± 2.08%. Degradation in solvent suffers no influence of NCs with 2% of NCs. Adhesives and primer presented controlled drug release. Indomethacin diffused through dentin. Adhesive and primer also presented an antimicrobial effect. The incorporation of NCs in adhesive and primer showed no influence on in situ DC and immediate bond strength compared to materials with no NCs. The use in combination of primer and adhesive with NCs resulted in higher contact angle and lower longitudinal bond strength. It is possible to conclude that the use adhesive with incorporation of NCs has potential to provide therapeutic effects on dentin adhesion.

Orientador: Caio Cézar Randi Ferraz
Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba
Made available in DSpace on 2018-08-17T10:36:37Z (GMT). No. of bitstreams: 1 AndradeJunior_CarlosVieira_M.pdf: 2836210 bytes, checksum: 3bec31e65b6116b6cf32dfeec80e725b (MD5) Previous issue date: 2010
Resumo: O objetivo deste estudo in vitro foi avaliar o selamento coronário e resistência de união do cimento resinoso AH Plus associado a um protocolo de hibridização da dentina radicular com Scotchbond Multi Purpose (SBMP) após o uso de diferentes substâncias químicas auxiliares endodônticas (Hipoclorito de Sódio 5,25%, Gluconato de Clorexidina 2%, EDTA 17% e ácido fosfórico 37%). Para avaliar o selamento, foram utilizadas raízes palatinas de molares superiores divididas em 18 grupos (n=10) que foram tratadas com diferentes substâncias químicas, obturadas com cimento endodôntico AH Plus associado a cones resinosos ou a cones de guta-percha. Em alguns grupos obturados com AH Plus + cones resinosos, a dentina foi hibridizada antes da aplicação do material obturador. O selamento coronário foi avaliado pelo método de filtração de fluidos. Um espécime de cada grupo foi levado ao MEV para avaliação morfológica da interface de união entre os materiais obturadores e a dentina radicular. Para a avaliação da resistência de união do cimento à dentina radicular foram utilizadas 60 raízes de dentes bovinos, cortadas longitudinalmente, que receberam tratamento com as substâncias químicas auxiliares utilizadas na avaliação do selamento (n=5). Foram criadas seis perfurações nas raízes selecionadas, duas por terço, onde foi inserido o cimento AH Plus, após o tratamento da dentina com o sistema adesivo SBMP. Após a presa do cimento, os corpos-de-prova foram submetidos ao teste de resistência ao cisalhamento por extrusão ?Push out?. Posteriormente, o modo de fratura foi analisado em lupa estereoscópica 32X. Um espécime de cada grupo foi avaliado no MEV para confirmação das análises feitas pela lupa. A análise do modo de fratura demonstrou (22,77%) fraturas adesivas, (11,67%) fraturas coesivas em cimento e (65,55%) fraturas mistas para o protocolo SBMP/ AH Plus, enquanto que para o AH Plus a distribuição foi (86,11%) coesivas em cimento e (13,89%) mistas. A análise estatística (Dixon-Grubbs-Neuman, Kolmogorov-Smirnov, Cochran e Tukey HSD) demonstrou que o selamento coronário, após a hibridização dentinária com o SBMP e obturação com cone Resinoso + AH Plus, foi superior ao promovido pela guta-percha associada ao AH Plus, para todos os protocolos de irrigação (p ? 0,05). Para a resistência de união, a aplicação do SBMP se mostrou desfavorável, pois diminuiu a resistência de união do AH Plus (p ? 0,05). As substâncias químicas agiram diferentemente sobre a resistência de união nos grupos onde foi aplicado o adesivo, sendo observado que o tratamento dentinário com clorexidina e soro apresentou melhores valores de resistência quando foram associados ao condicionamento dentinário com EDTA 17%, diferentemente do que ocorreu nos grupos onde se aplicou hipoclorito de sódio 5,25% que apresentou melhores resultados com a utilização do ácido fosfórico 37%. Houve correlação inversa entre resistência de união e capacidade de selamento. Pode-se concluir que o uso do sistema adesivo Scotchbond Multi Purpose melhorou a capacidade de selamento coronário do AH Plus para todos os protocolos de irrigação utilizados, e que a resistência de união deste cimento foi diminuída quando o adesivo foi aplicado, sendo influenciada pelo tipo de condicionamento e substâncias químicas
Abstract: The aim of this in vitro study was to evaluate the sealing ability and bond strength of AH Plus sealer associated with a hybridization protocol of root dentin with ScotchbondMulti Purpose (SBMP) after the use to different endodontic auxiliary chemical substances (5.25% sodium hypochlorite and 2% Chlorhexidine and 17 EDTA) in One hundred-eighty palatal roots of maxillary molars were selected and divided into 18 groups according to the dentin protocol treatment (n=10), filled with AH Plus sealer associated with resinous cones or gutta-percha in order to evaluate the sealing ability by fluid filtration (FLODEC system). In s groups that were used in the AH Plus + resinous cones, was hybridized dentin before applying the sealing material. One specime from each group was taken to a SEM morphology analysis of the bonded interfaces between sealers and dentin. For the bond strength test, 60 root bovine teeth were selected and treated with each auxiliary chemical substances selected (n=5). Six holes were poked in each root, being two in the cervical, middle and apical third of the root. The roles were filled with AH Plus sealer with or without the adhesive system, and subsequently, submitted to push out test. Thereafter, the fracture mode was examined using stereomicroscope (x32). One specimen from each was SEM analyzed. The fracture mode methodology revealed a 22.77% of adhesive, 11.67% of cohesive and 65.55% of mixture fracture for the SBMP / AH Plus protocol. In contrast, the AH Plus protocol indicated 86.11% of cohesive and 13.89% of mixed fracture. Statistical analysis (Dixon-Grubs-Neuman, Kolmogorov-Smirnov, Cochran and Tukey HSD) showed that the ScotchBond Multi Purpose (SBMP) + Resilon cone + AH Plus sealer group promoted a higher sealing ability than the gutta-percha + AH Plus sealer group (p < 0.05), regardless the auxiliary chemical substance. The bond strength were lower with the SBMP application than without its use (p<0.05). The chemicals acted differently on the bond strength in groups where the adhesive was applied, we observed that the dentin treatment with chlorhexidine and serum values showed better resistance when they were associated with dentin conditioning with 17% EDTA, unlike what occurred in the groups where sodium hypochlorite is applied, that it was found better results with the use of phosphoric acid 37%. A reverse correlation was found between bond strength and sealing ability. Was concluded that the use of adhesive system Scotchbond Multi Purpose improved coronal sealing ability of AH Plus for all protocols used irrigation, and that the bond strength of cement was reduced when the adhesive was applied, being influenced by type conditioning and chemicals substances.
Mestrado
Endodontia
Mestre em Clínica Odontológica

A presente pesquisa se propôs a avaliar a influência de cinco tratamentos dentinários na resistência de união à dentina de quatro cimentos de ionômero de vidro modificados por resina (CIVRMs). O ensaio experimental foi realizado in vitro, fazendo uso de 200 incisivos bovinos. Destes, foram obtidos 200 fragmentos de dentina, que foram distribuídos aleatoriamente em 20 grupos (n=10), segundo os fatores de variação que compreendem cinco tratamentos dentinários (Grupo controle, ou seja, sem tratamento; Ácido Poliacrílico a 20%, Clearfil SE Bond; Single Bond Universal e Primer do Vitremer) e quatro cimentos ionoméricos (GC Fuji II LC® CAPSULE; GC Fuji LINING® LC (Paste Pak); Vitrebond® e Vitremer). Após a confecção dos corpos de prova e 24h de armazenamento em estufa à 37oC, foi realizado o teste de microcisalhamento na máquina de ensaios universal (Instron 5942 - Canton, MA, EUA) com velocidade de 1mm/min, seguido da análise do padrão de fratura em microscópio digital. A análise estatística dos 400 resultados obtidos foi feita por meio do teste paramétrico ANOVA para dois fatores de variação (cimento e tratamento) (p<0,05%) e pelo teste auxiliar de Tukey (p<0,05%). Os testes estatísticos demonstraram haver diferença estatística tanto entre os tratamentos, como entre os cimentos e na interação de ambos (p<0,0001). Os sistemas adesivos Clearfil SE (X?=18,26 ± 2,78) e SingleBond (X?=17,28 ± 2,49) promoveram os valores de resistência adesiva mais elevados em comparação aos demais tratamentos, mas sem apresentarem diferença estatística entre si, o que representou um aumento na resistência de união de 121% para o Clearfil SE e 109,2% para o Single Bond Universal em relação ao Grupo Controle. O uso do Ácido Poliacrílico (X?=9,94 ± 3,55) alcançou valores intermediários, correspondendo a um aumento de 20% na resistência adesiva em relação ao Grupo Controle. Esse tratamento se diferenciou estatisticamente dos maiores valores, porém não apresentou diferença frente ao Primer do Vitremer (X?=8,91 ± 2,97). O grupo controle (X?=8,26 ± 4,17) evidenciou os menores valores, se diferenciando estatisticamente dos sistemas adesivos e do Ácido Poliacrílico, mas com resultados que o equiparou ao tratamento com o Primer do Vitremer. Ao se analisar a interação entre cimento e tratamento, todos os cimentos de ionômero de vidro resinomodificados (CIVRMs) testados neste estudo apresentaram seus maiores resultados quando um dos sistemas adesivos foi utilizado como tratamento dentinário, independente de qual sistema adesivo. Com base nesses resultados, pôde-se concluir que os dois sistemas adesivos autocondicionantes foram capazes de melhorar significativamente a resistência adesiva dos CIVRMs.
This research aims to evaluate the influence of five dentin pretreatments on microshear bond strength of four resin-modified glass ionomer (RMGI). The experiment was performed in vitro, using 200 bovine incisors. From these, there were obtained 200 dentine fragments that were randomly distributed into 20 groups (n = 10) according to the variation factors comprising five dentin treatment (control group, i.e., no treatment; Polyacrylic Acid 20%; Clearfil SE Bond; Single Bond Universal and Vitremer Primer) and four glass ionomer cements (GC Fuji II LC® CAPSULE; GC Fuji LC LINING® (Paste Pak); Vitrebond® and Vitremer). After preparation of the samples and 24h storage at 37 °C, was performed microshear test in a universal testing machine (Instron 5942 - Canton, MA, USA) with speed of 1mm/min, followed by analysis of the pattern fractures in digital microscope. Statistical analysis of the 400 results was performed by ANOVA nonparametric test for two variation factors (cement and treatment) (p <0.05%) and the post-hoc Tukey (p <0.05%). The tests demonstrated there are statistical difference between treatments, cements and between the interaction of both (p <0.0001). The Clearfil SE (X?=18,26 ± 2,78) and SingleBond (X?=17,28 ± 2,49) promoted the highest bond strength values compared to the other treatments, but showing no statistical difference between them, which represented an increase in bond strength of 121% for Clearfil SE and 109.2% for Single Bond Universal compared to control group. The Polyacrylic Acid (X?=9,94 ± 3,55) has reached intermediate values, corresponding to a 20% increase in adhesive strength compared to control group. This treatment differed significantly from the higher values, but showed no difference compared to Primer Vitremer (X?=8,91 ± 2,97). The control group (X?=8,26 ± 4,17) showed the lowest values, statistically differing from the adhesives and polyacrylic acid, but with results that matched to the treatment with Vitremer Primer. When analyzing the interaction between cement and treatment, all cements tested in this study had higher results when one of the adhesive systems was used as dentin treatment, regardless of which adhesive system. Based on these results, it could be concluded that the two adhesive systems were able to significantly improve the adhesive strength of RMGIs.

Made available in DSpace on 2017-07-24T19:22:10Z (GMT). No. of bitstreams: 1 Yasmine Bitencourt Emilio Mendes.pdf: 6295050 bytes, checksum: ec73165b3475fb2d502d87ebf6e6717e (MD5) Previous issue date: 2010-02-11
Coordenação de Aperfeiçoamento de Pessoal de Nível Superior
The aim of this study was to assess the effect of different modes of application of a conventional adhesive system AdperTM Single Bond [SB] and of two self-etch adhesives AdperTM SE Plus [SE] and AdheSE® [AD] and influence of dentin depth on mechanical properties of hardness and elastic modulus of adhesive layer using the nanoindentation technique. The surfaces occlusal of 48 caries-free human third molars were removed and the smear layer standardized for the obtaining of a flat superficial dentin surface, in two levels: superficial dentine (DS) or deep dentine (DP). The adhesives were applied on the dentin surface in two layers, under active (AA) or passive (PA) application and photoactivated (10 s / 500 mW/cm2). After composite build-ups were constructed incrementally and were stored in water by 24 h. The teeth were sectioned in perpendicular direction to obtain specimens in form of bonded sticks with a cross-sectional area of 0.8 ± 0.1mm2, separating the central bonded sticks of each tooth for they be fastened in sample holder and metallographic polishing. The test of nanoindentation was made on composite resin, adhesive system and dentin regions. The results of hardness and elastic modulus (GPa) of adhesive layer were analyzed by a three-way ANOVA and Tukey’s multiple comparison tests (α=0.05) and also took place the two-way ANOVA for each adhesive separately. The mean and standard deviation of hardness and elastic modulus values of composite resin (GPa) were respectively (0.94 ± 0.05) and (13.41 ± 0.52). In dentin, the hardness was (0.89 ± 0.06) and the elastic modulus (17.51 ± 0.71). In the adhesive layer, the highest hardness (0.32 ± 0.02) and elastic modulus (5.54 ± 0.47) of SB were obtained in DS group. The elastic modulus in the adhesive layer of SE (4.11 ± 0.10) was lowest in AA group. For the adhesive layer of AD, just the mode of application was statistically significant (p=0.0041), being AA (0.29 ± 0.01) larger than PA (0.26 ± 0.01) (p=0.0042). It was concluded that: 1) passive application in superficial dentine got greaters values of hardness and modulus of elasticity of the SB and of SE, 2) the active application in deep dentine resulted in bigger values of the properties in study of SB, 3) active application significantly influenced the values of hardness in the area of the adhesive layer of the AD ones in such a way in superficial dentine how much in deep, but didn’t influence the modulus.
O objetivo deste trabalho foi avaliar o efeito da forma de aplicação do sistema adesivo convencional AdperTM Single Bond 2 [SB] e dos sistemas adesivos autocondicionantes AdperTM SE Plus [SE] e AdheSE® [AD] e da profundidade dentinária nas propriedades mecânicas de dureza e módulo de elasticidade da camada adesiva por meio do teste de nanoindentação. As superfícies oclusais de 48 terceiros molares humanos hígidos foram seccionadas e a smear layer padronizada para a obtenção de uma superfície dentinária plana, em dois níveis: dentina superficial (DS) ou dentina profunda (DP). Os adesivos foram aplicados sobre a superfície dentinária em duas camadas de forma ativa (AA) ou forma passiva (AP) e fotoativados (10 s / 500 mW/cm2). Em seguida, foram restaurados incrementalmente e armazenados em água destilada por 24h. Os dentes foram seccionados em eixos “x” e “y” para obtenção de espécimes em forma de palitos de aproximadamente 0,8 + 0,1 mm2 de secção transversal, separando o palito central de cada dente para serem fixados em porta-amostra e polidos metalograficamente. O teste de nanoindentação foi realizado nas regiões da resina composta, camada adesiva e dentina. Os valores de dureza e módulo de elasticidade (GPa) da camada adesiva foram submetidos a uma análise de variância de três fatores e ao teste de Tukey para contraste das médias (α=0,05), e também realizou-se a análise de variância de 2 fatores para cada adesivo isoladamente. As médias e os desvios padrões da dureza e do módulo de elasticidade (GPa) da resina composta foram respectivamente (0,94 ± 0,05) e (13,41 ± 0,52). Em dentina, a dureza foi (0,82 ± 0,06) e o módulo de elasticidade (17,51 ± 0,71). Para o grupo do SB na camada adesiva, os maiores valores de dureza (0,32 ± 0,02) e módulo de elasticidade (5,54 ± 0,47) foram obtidos no grupo DS. O módulo de elasticidade da camada adesiva do SE (4,11 ± 0,10) foi menor para o grupo AA. Para a região da camada adesiva do AD, apenas a forma de aplicação foi estatisticamente significante (p=0,0041), sendo a AA (0,29 ± 0,01) maior que a AP (0,26 ± 0,01) (p=0,0042). Concluiu-se que: 1) aplicação passiva em dentina superficial obteve maiores valores de dureza e módulo de elasticidade do SB e do SE, 2) a aplicação ativa em dentina profunda resultou em maiores valores das propriedades em estudo do SB, 3) aplicação ativa influenciou significativamente os valores de dureza na região da camada adesiva do AD tanto em dentina superficial quanto em profunda, porém não influenciou o módulo de elasticidade.

Made available in DSpace on 2014-06-11T19:24:07Z (GMT). No. of bitstreams: 0 Previous issue date: 2011-06-29Bitstream added on 2014-06-13T20:31:05Z : No. of bitstreams: 1 torres_lms_me_sjc.pdf: 1289584 bytes, checksum: a62d84cf9380d80ba27b908f64260c42 (MD5)
Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
Este estudo in vitro teve como objetivo avaliar a influência das ciclagens térmica e termomecânica na resistência adesiva de bráquetes colados em esmalte bovino com primers convencionais e auto-condicionates. Noventa incisivos bovinos foram aleatoriamente divididos em 2 grupos (G), de acordo com o primer utilizado: XT (n=45) – bráquetes colados com primer convencional (Transbond XT/3M, Unitek); SEP (n=45) – bráquetes colados com primer auto-condicionante (Transbond Plus SEP/3M, Unitek). Após a colagem dos bráquetes, cada grupo foi subdividido em 3 subgrupos (n=15): SC (sem ciclagem) – as amostras não receberam nenhum tipo ciclagem; CT (ciclagem térmica) – as amostras receberam apenas ciclagem térmica (500 ciclos de 50C a 550C); CTM (ciclagem termomecânica) – as amostras receberam ciclagem termomecânica (100.000 ciclos de 50C a 550C). A seguir, foi realizado o teste de cisalhamento em uma máquina de ensaios universal (EMIC) a uma velocidade de 1mm/min com célula de carga de 100kg. Após o descolamento dos bráquetes, amostras de cada grupo foram submetidas à avaliação microscópica em microscópio eletrônico de varredura, a fim de analisar a superfície do esmalte e quantificar o Índice de Adesivo Remanescente (IAR) sobre a superfície. Os resultados mostraram que o grupo SEP apresentou maior resistência adesiva (14,70±4,85 MPa) quando comparado com o grupo XT (11,27±4,48 MPa). Para os grupos XT, a resistência adesiva manteve-se semelhante independente do tipo de ciclagem (SC, 11,44 MPa; CT, 11,20 MPa; CTM,11,19 MPa), enquanto que para os grupos SEP o subgrupo CTM foi o que apresentou maiores valores de resistência adesiva (16,84 MPa), seguido do CT (14,99 MPa) e SC (12,26 MPa). O teste ANOVA - 2 fatores revelou que o efeito interação não é estatisticamente significante; indicando, assim, que o efeito do tipo de ciclagem para o grupo XT é o mesmo...
The aim of this in vitro study was to evaluate the influence of thermal and thermomechanical cycling on shearbond strength of orthodontic brackets bonded with conventional and self-etching primers. 90 bovine incisors were randomly divided into 2 groups (G) according to the primer: XT (n=45) – brackets bonded with conventional primer (Transbond XT/3M, Unitek); SEP (n=45) – brackets bonded with self-etching primer (Transbond Plus SEP/3M, Unitek). After bonding, each group were divided into 3 subgroups (n=15): NC (no cycling) – the specimens did not receive any kind of cycling; TC (thermal cycling) – the specimens received only thermal cycling (500 cycles); TMC (thermomechanical cycling) – the specimens received thermomechanical cycling (100.000 cycles). Next, the shearbond strength test was performed in a universal testing machine (EMIC) at a crosshead speed of 1mm/min. After debonding, specimens of each group were submitted to microscopic evaluation in order to analyze the enamel surface, the adhesive penetration and quantify the Adhesive Remaining Index (ARI). The results showed that the SEP group presented higher bond strength (14,70±4,85 MPa) compared with XT (11,27±4,48 MPa). For XT, the bond strength remained similar despite cycling (NC, 11,44 MPa; TC, 11,20 MPa; TMC,11,19 MPa), meanwhile for SEP, the subgroup TMC showed higher values of bond strength (16,84 MPa), followed by TC (14,99 MPa) e NC (12,26 MPa). 2-way ANOVA test indicated that the interaction effect is not statistically different, so the kind of cycling effect for XT is equal for SEP. But the primer effect (XT vs SEP) is statiscally significant. According to the ARI , the group that presented the highest remaining adhesive on the enamel surface was SEP/TMC (ARI=3). The results showed that self-etching primers can be safely used in orthodontic practice because presents adequate values of bond strength ... (Complete abstract click electronic access below)

Este estudo teve como objetivo analisar o efeito da contaminação por saliva humana na resistência de união (RU) da interface adesiva em dentina por microtração, nas características morfológicas da camada híbrida (CH) em microscopia confocal e no grau de conversão (GC) de 2 sistemas adesivos: Adper Single bond 2 (SB) e Single Bond® Universal (SU). Cento e oitenta dentes terceiros humanos hígidos foram divididos em 12 grupos (n=10), de acordo com o sistema adesivo utilizado, a presença de saliva e o tempo de armazenagem. Após o procedimento adesivo e aplicação da resina composta Filtek Z250, os dentes foram mantidos em água destilada em estufa a 37°C por 48 horas, 6 meses ou 12 meses antes de serem seccionados em palitos (0,8mm x 0,8mm, aproximadamente) para serem levados à máquina de ensaios universal Instron para os testes de microtração. Para à análise da interface adesiva em microscopia confocal de varredura a laser para verificação e mensuração de alterações internas na interface foram utilizados 60 dentes divididos em 6 grupos (n=10) de acordo com os tempos de 48 horas, 6 meses, e 12 meses respectivamente, empregando os sistemas adesivos (SB) e (SU). O efeito da presença de saliva também foi avaliado pelo grau de conversão dos adesivos, empregando-se espectroscopia de infravermelho transformada de Fourier empregando os sistema adesivos (SB) e (SU) com incorporação de saliva humana na sua composição (n=5) com concentrações 10%, 25% e 50% em vol. Para a comparação das variáveis: RU, (GC), espessura da CH, na presença de saliva e tempo de armazenamento foram utilizados os testes de Análise de Variância a três critérios e de comparações múltiplas de Tukey (p<0,05). Os valores de RU (MPa±dp: 48horas/6meses/1ano) foram: SB (43,53 ±6,0; 40,10±3,4; 38,59±5,4); SalSB (43,09±6,2; 39,86±6,6; 37,255,8); SU (42,98±4,3; 39,30±3,6; 40,44±5,7); Sal SU (44,39±4,2; 42,26±2,5; 38,26±5,7). Os Valores médios da CH (MPa±dp: 48horas/6meses/1ano) foram: SalSB (3,59±0,8; 3,59±1,0; 2,08±1,5). SalSU (1,26±0,5; 1,73±0,8; 1,07±0,3). Os valores de GC (MPa±dp: 10%/25%/50%vol) foram: SB (85,59±3,4; 49,68±12,8; 38,56±11,8); SU (85,52±3,3; 86,27±3,5; 57,82±11,1).Conclui-se, portanto, que a contaminação por saliva humana não interferiu na RU da interface dentina/resina composta após 48 horas, 6 meses e 12 meses. A morfologia da camada hibrida foi alterada pela presença da saliva nos períodos 6 e 12 meses,. O GC dos sistemas adesivos foi afetado pela presença de saliva após a polimerização imediata. Entretanto o fator tempo foi determinante para a deformação da interface dentina/resina para ambos os sistemas adesivos.
The objective of this study was to analyze the effect of human saliva contamination on bond strength of the dentin/adhesive interface, morphology of the hybrid layer by confocal microscopy and SEM analysis and degree of conversion of 2 adhesive systems: Adper Single bond 2 (SB) and Single Bond® Universal ( SU). One hundred and eighty healthy human third teeth were divided into 12 groups (n = 10), according to the adhesive system used, the presence of saliva and the storage time. After the adhesive procedure and placement of resin composite (Filtek Z250), the teeth were stored in distilled waterat 37 ° C for 48 hours, 6 months or 12 months before being cut into sticks (0.8mm x 0.8mm, approximately) to the microtensile strength tests. For the analysis of the adhesive interface in confocal microscopy of laser scanning for verification and measurement of internal interface changes, 60 teeth were used divided into 6 groups (n = 10) according to the storage time: 48 hours, 6 months, and 12 monthsand (SB) and (SU). The effect of the presence of saliva was also evaluated by the degree of conversion of the adhesives using Fourier transform infrared spectroscopy employing adhesive (SB) and (SU) systems incorporating human saliva in its composition (n = 5) with 10%, 25% and 50% vol. For the comparison of the variables: bond strength, degree of conversion, and hybrid layer thickness in the presence of saliva and storage time, the three criteria Variance Analysis and Tukey multiple comparisons tests (p <0.05) were used. The values of bond strength (MPa ± dp: 48hours / 6meses / year) were: SB (43.53 ± 6.0, 40.10 ± 3.4, 38.59 ± 5.4); SalSB (43.09 ± 6.2, 39.86 ± 6.6, 37.255.8); SU (42.98 ± 4.3, 39.30 ± 3.6, 40.44 ± 5.7); SU salt (44.39 ± 4.2, 42.26 ± 2.5, 38.26 ± 5.7). The mean values of hybrid layer thickness (MPa ± dp: 48hours / 6meses / year) were: SalSB (3.59 ± 0.8, 3.59 ± 1.0, 2.08 ± 1.5). SalSU (1.26 ± 0.5, 1.73 ± 0.8, 1.07 ± 0.3). The values of degree of conversion (MPa ± dp: 10% / 25% / 50% vol) were: SB (85.59 ± 3.4, 49.68 ± 12.8, 38.56 ± 11.8); (85.52 ± 3.3, 86.27 ± 3.5, 57.82 ± 11.1). It was therefore concluded that human saliva contamination did not interfere on bond strength of the dentin/adhesive interface after 48 hours, 6 months and 12 months. The morphology of the hybrid layer was altered by the presence of saliva after 6 and 12 months. The degree of conversion of adhesive systems was affected by the presence of saliva immediately after polymerization. However, the time factor was determinant for the dentine/resin interface deformation for both adhesive systems.

Submitted by Caroline Xavier (caroline.xavier@pucrs.br) on 2017-05-23T17:19:03Z No. of bitstreams: 1 DIS_BIANCA_MORO_CORREA_PARCIAL.pdf: 139620 bytes, checksum: 7b6664e8dedb350b29c7a7898c664250 (MD5)
Made available in DSpace on 2017-05-23T17:19:03Z (GMT). No. of bitstreams: 1 DIS_BIANCA_MORO_CORREA_PARCIAL.pdf: 139620 bytes, checksum: 7b6664e8dedb350b29c7a7898c664250 (MD5) Previous issue date: 2017-01-19
Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior - CAPES
Objectives: The aims of this study were to evaluate the elastic modulus and the monomer conversion of self- etching adhesives (Single Bond Universal and Clearfil SE Bond) and two- steps etch-and-rinse adhesives (primer + adhesive in the same bottle, Adper Single Bond 2 and Gluma 2Bond). The null hypothesis was that two-step adhesive systems will have higher degree of monomer conversion and a higher elastic modulus than the self-etching ones. Materials and methods: On dentin disks obtained from 10 extracted third molars were applied self- etching and etch-and-rinse adhesive systems according to manufacturer's instructions and light cured by a LED light. Right after, the specimens were submitted to elastic modulus by atomic force with 50g load for 10s. The degree of conversion of the adhesives was calculated by Fourier Transform Infrared Spectroscopy (FTIR). Results: The Single Bond 2 adhesive system presented the highest monomer conversion result (88%) followed by Universal Single Bond (79%), Gluma 2Bond (71%) and Clearfil SE Bond (69%). The results for elastic modulus (MPa) were (means followed by the same letter did not present statistical difference for Tukey (p?0,05)): Single Bond 2, 2319 (A); Single Bond Universal, 2051 (AB); Gluma, 2038 (AB); Clearfil SE Bond, 1788 (B). Conclusion: lt is not possible to infer that, as a rule, conventional adhesives systems with combined primer and adhesives will have a better performance in terms of the degree of monomer conversion as well as modulus of elasticity when compared to self-etching agents.
Objetivos: Este trabalho teve por objetivos avaliar o m?dulo de elasticidade e a taxa de convers?o de mon?meros de sistemas adesivos autocondicionantes (Single Bond Universal e Clearlil SE Bond) e convencionas de dois passos (primer+adesivo no mesmo frasco, Adper Single Bond 2 e Gluma 2Bond). A hip?tese inicial foi que os sistemas adesivos de dois passos ter?o maior grau de convers?o de mon?meros e maior m?dulo de elasticidade que os autocondicionantes. Materiais e m?todos: sobre discos de dentina obtidos a partir de 10 molares extra?dos foram aplicados os sistemas adesivos de condicionamento ?cido total e os autocondicionantes de acordo com a recomenda??o dos fabricantes de cada material e fotoativados com luz LED. Ap?s, os corpos de prova foram submetidos ? medi??o de m?dulo de elasticidade por for?a at?mica com carga de 50g pelo tempo de 10s. O grau de convers?o dos adesivos foi calculado usando espectroscopia por infravermelho (FTIR). Resultados: O sistema adesivo Single Bond 2 apresentou o maior resultado de convers?o de mon?meros (88%) seguido do Single Bond Universal (79%), Gluma (71%) e Cleartil SE Bond (69%). Os resultados para o m?dulo de elasticidade (MPa) foram (m?dias seguidas de mesma letra n?o apresentam diferen?a estat?stica para Tukey (p?0,05)): Single Bond 2, 2319(A); Single Bond Universal, 2051(AB); Gluma, 2038(AB); Clearfil SE Bond, 1788(B). Conclus?o: N?o ? poss?vel inferir que via de regra pelo fato de serem os sistemas adesivos convencionais com primer e adesivos combinados ter?o um melhor desempenho quanto ao grau de convers?o de mon?meros bem como m?dulo de elasticidade quando comparados aos autocondicionantes.

Orientador: Rebeca Di Nicoló
Banca: Clovis Pagani
Banca: Daniela Raggio
Resumo: Este estudo in vitro teve como objetivo avaliar a influência das ciclagens térmica e termomecânica na resistência adesiva de bráquetes colados em esmalte bovino com primers convencionais e auto-condicionates. Noventa incisivos bovinos foram aleatoriamente divididos em 2 grupos (G), de acordo com o primer utilizado: XT (n=45) - bráquetes colados com primer convencional (Transbond XT/3M, Unitek); SEP (n=45) - bráquetes colados com primer auto-condicionante (Transbond Plus SEP/3M, Unitek). Após a colagem dos bráquetes, cada grupo foi subdividido em 3 subgrupos (n=15): SC (sem ciclagem) - as amostras não receberam nenhum tipo ciclagem; CT (ciclagem térmica) - as amostras receberam apenas ciclagem térmica (500 ciclos de 50C a 550C); CTM (ciclagem termomecânica) - as amostras receberam ciclagem termomecânica (100.000 ciclos de 50C a 550C). A seguir, foi realizado o teste de cisalhamento em uma máquina de ensaios universal (EMIC) a uma velocidade de 1mm/min com célula de carga de 100kg. Após o descolamento dos bráquetes, amostras de cada grupo foram submetidas à avaliação microscópica em microscópio eletrônico de varredura, a fim de analisar a superfície do esmalte e quantificar o Índice de Adesivo Remanescente (IAR) sobre a superfície. Os resultados mostraram que o grupo SEP apresentou maior resistência adesiva (14,70±4,85 MPa) quando comparado com o grupo XT (11,27±4,48 MPa). Para os grupos XT, a resistência adesiva manteve-se semelhante independente do tipo de ciclagem (SC, 11,44 MPa; CT, 11,20 MPa; CTM,11,19 MPa), enquanto que para os grupos SEP o subgrupo CTM foi o que apresentou maiores valores de resistência adesiva (16,84 MPa), seguido do CT (14,99 MPa) e SC (12,26 MPa). O teste ANOVA - 2 fatores revelou que o efeito interação não é estatisticamente significante; indicando, assim, que o efeito do tipo de ciclagem para o grupo XT é o mesmo ... (Resumo completo, clicar acesso eletrônico abaixo)
Abstract: The aim of this in vitro study was to evaluate the influence of thermal and thermomechanical cycling on shearbond strength of orthodontic brackets bonded with conventional and self-etching primers. 90 bovine incisors were randomly divided into 2 groups (G) according to the primer: XT (n=45) - brackets bonded with conventional primer (Transbond XT/3M, Unitek); SEP (n=45) - brackets bonded with self-etching primer (Transbond Plus SEP/3M, Unitek). After bonding, each group were divided into 3 subgroups (n=15): NC (no cycling) - the specimens did not receive any kind of cycling; TC (thermal cycling) - the specimens received only thermal cycling (500 cycles); TMC (thermomechanical cycling) - the specimens received thermomechanical cycling (100.000 cycles). Next, the shearbond strength test was performed in a universal testing machine (EMIC) at a crosshead speed of 1mm/min. After debonding, specimens of each group were submitted to microscopic evaluation in order to analyze the enamel surface, the adhesive penetration and quantify the Adhesive Remaining Index (ARI). The results showed that the SEP group presented higher bond strength (14,70±4,85 MPa) compared with XT (11,27±4,48 MPa). For XT, the bond strength remained similar despite cycling (NC, 11,44 MPa; TC, 11,20 MPa; TMC,11,19 MPa), meanwhile for SEP, the subgroup TMC showed higher values of bond strength (16,84 MPa), followed by TC (14,99 MPa) e NC (12,26 MPa). 2-way ANOVA test indicated that the interaction effect is not statistically different, so the kind of cycling effect for XT is equal for SEP. But the primer effect (XT vs SEP) is statiscally significant. According to the ARI , the group that presented the highest remaining adhesive on the enamel surface was SEP/TMC (ARI=3). The results showed that self-etching primers can be safely used in orthodontic practice because presents adequate values of bond strength ... (Complete abstract click electronic access below)
Mestre

The bond strength may be influenced by the different composition and manipulation of the adhesive systems, the dentin structure and the method of evaluation. After exposure of the occlusal dentin surface 160 third human molars were divided in 2 groups (n=80) for the micropush-out (μPBS) and microshear (μSBS) bond strength tests. For the μPBS, 4 groups (n=20) were obtained and a tapered cavity (2,5x1,5x1,0mm) was prepared on the dentin surface and restored with composite resin after treatment using different adhesive systems: Adper Single Bond, Adper Scotchbond MP, Prompt-L-Pop, AdheSE. After water storage for 24 hours, from 10 teeth per group, 1 oclusal slice (1,5 ±0,3mm) was obtained from each tooth, and the restoration submitted to vertical load. The other 10 teeth were storage for 12 months and then submitted to the same procedure. For the μSBS another 80 teeth were divided into 4 groups (n=20), the dentin surface was treated using the same adhesive systems and composite resin cylinders (1x1mm) were constructed and polymerized in a single increment onto the bonding area. Ten specimens were tested after 24 hours and 10 after 12 months of water storage. The null hypotheses were that (1) the composition and manipulation of the adhesive systems, (2) the water storage and (3) the method of evaluation might influence the bond strength of direct composite resin restorations. Results of ANOVA did not show significant difference for the storage time factor (p=.6343), but there was difference between the methods (p<.0001), with higher values for the μPBS test, and among the adhesive systems (p<.0001). The Adper Scotchbond and AdheSE systems presented higher bond strength values. Adhesive x method (p=.0002) and adhesive x method x time (p=.0037) interactions were significant, with different behaviors from adhesive systems within the method and time of evaluation. Conclusions were that the storage time might be not sufficient to result in alterations and that adhesive systems composition and manipulation might influence the bond strength. The μPBS test, presented the higher bond values with lower coefficient of variation, indicating more consistence than the μSBS test, besides of reproduce more faithfully clinical conditions.
Dentre os vários fatores que podem influenciar a resistência adesiva de diferentes sistemas adesivos à dentina estão as suas diferentes composições e manipulação, o substrato dentinário e a produção do teste. Após exposição da superfície dentinária oclusal 160 molares humanos foram divididos em 2 grupos (n=80) para os testes de micropush-out e micro-cisalhamento. Para o teste de micropush-out a superfície dentinária de 4 grupos (n=20) recebeu uma cavidade tronco-cônica (2,0x1,5x1,0mm) restaurada com resina composta após aplicação do sistema adesivo: Adper Single Bond (SLB); Adper Scotchbond MP (SMP); Prompt-L-Pop (PLP); Adhe SE (ADH). Após armazenagem em água por 24 horas, a partir de 10 dentes de cada grupo, foi obtida uma fatia oclusal (1,5 ±0,3mm) por dente cuja restauração foi submetida à carga vertical. Os outros 10 dentes de cada grupo foram armazenados por um ano e submetidos ao mesmo procedimento. Para o teste do micro-cisalhamento outros 80 dentes foram divididos em 4 grupos (n=20), a superfície dentinária foi tratada com os mesmos sistemas adesivos, e, diretamente sobre ela, cilindros de resina (1x1 mm) foram construídos e polimerizados em incremento único. Dez amostras de cada grupo foram testadas após 24 horas e as outras após um ano de armazenagem. As hipóteses nulas foram que (1) a composição e manipulação dos sistemas adesivos, (2) a armazenagem em água, e (3) o método de avaliação, não influenciam a resistência de união das restaurações de resina composta direta. A ANOVA não mostrou diferença significante para o fator tempo de armazenagem (p=0,6343), mas houve diferença entre os métodos de avaliação (p<0,0001), com valores mais altos para o micropush-out, e entre os adesivos (p<0,0001). O Adper Scotchbond MP e AdheSE apresentaram resultados melhores que os outros sistemas testados. As interações adesivos x métodos (p=0,0002) e adesivos x métodos x tempo (p=0,0037) foram significativas com comportamentos diferentes dos adesivos dentro do método e do tempo de armazenagem. Os resultados indicaram que a composição e manipulação dos adesivos influenciaram a resistência de união. O método micropush-out, além de resultar em valores mais altos de união, apresentou também menor coeficiente de variação, indicando ser mais consistente que o microcisalhamento, além de simular mais fielmente as condições clínicas. O tempo de armazenagem avaliado pode não ter sido suficiente para promover alteração que pudesse ser identificada no teste de resistência adesiva.
Mestre em Odontologia

The aim of this study was to evaluate the influence of different adhesive systems in the color of resin composites with different translucency. Sixty specimens of resin composite, in the shades A2 (n=30) e OA2 (n=30) were made with aid of a metallic mould with 8 mm of intern diameter and 1.25 mm of thickness, and randomly divided according to the adhesive system: two-step etch-and-rinse (Adper Single Bond 2; 3M ESPE), two-step self-etch (Clearfil SE Bond; KURARAY) and universal (Single Bond Universal; 3M ESPE). The materials were applied on the surface of the disk-shaped specimens, simulating direct restorations. The color evaluations were measured with spectrophotometer immediately after the polishing the specimens and after the application of the adhesive systems. The data of CIE L*a*b* system were used for the calculus of ΔE, ΔL, Δa e Δb. Additionally, 5 specimens of each adhesive system were made with the same dimensions of the disks of resin composite for measurement of the L*, a* e b* parameters. The data obtained were subjected to Analysis of Variance and Tukey test (5%). The application of the adhesive system Single Bond Universal on resin composite A2 resulted in highest color change p= 0.000; ΔE = 3.1 ± 0.7). No statistical significant difference was observed among adhesive systems when applied on resin composite shade OA2 (p>0.05). The universal adhesive showed higher trend to green and yellow. In conclusion, the effect of the adhesive system is material-dependent. The adhesive Single Bond Universal results in higher color change when a resin composite with higher translucency is used.
O objetivo deste estudo foi avaliar a influência de diferentes sistemas adesivos na cor de resinas compostas com diferentes translucidez. Sessenta corpos de prova de resina composta Z250 XT (3M ESPE), nas cores A2 (n=30) e OA2 (n=30) foram confeccionados com auxílio de uma matriz metálica com 8 mm de diâmetro interno e 1,25 mm de espessura e divididos aleatoriamente de acordo com o sistema adesivo: convencional de dois passos (Adper Single Bond 2; 3M ESPE), autocondicionante de dois passos (Clearfil SE Bond; KURARAY) e universal (Single Bond Universal; 3M ESPE). Os materiais foram aplicados sobre a superfície dos corpos de prova, simulando restaurações diretas. As avaliações de cor foram mensuradas com espectrofotômetro imediatamente após o polimento dos corpos de prova e posteriormente à aplicação dos sistemas adesivos. Os dados do sistema CIE L*a*b* foram utilizados para o cálculo do ΔE, ΔL, Δa e Δb. Adicionalmente, 5 corpos de prova de cada sistema adesivo foram confeccionados com as mesmas dimensões dos corpos de prova de resina composta para mensuração dos parâmetros L*, a* e b*. Os dados obtidos foram submetidos à Análise de Variância e Teste de Tukey (5%). A aplicação do sistema adesivo Single Bond Universal sobre a resina composta A2 resultou em maior alteração de cor (p = 0,000; ΔE = 3,1 ± 0,7). Nenhuma diferença estatisticamente significante foi observada entre os sistemas adesivos quando aplicados sobre a resina composta cor OA2 (p>0,05). O adesivo universal apresentou maior tendência para o verde e para o amarelo. Em conclusão, o efeito do sistema adesivo na cor das resinas compostas é material dependente. O adesivo Single Bond Universal resulta em maior alteração de cor quando uma resina com maior translucidez é utilizada.

Projeto de Pós-Graduação/Dissertação apresentado à Universidade Fernando Pessoa como parte dos requisitos para obtenção do grau de Mestre em Medicina Dentária
Todos os adesivos consistem em produtos desenvolvidos para realizarem a ligação entre os determinados materiais restauradores e a união aos tecidos dentários. Os adesivos autocondicionantes foram introduzidos recentemente no mercado e apresentam uma estratégia adesiva baseada na ação dos monómeros acídicos que condicionam simultaneamente os substratos dentários. O condicionamento acídico total é a base dos agentes adesivos contemporâneos, ou seja, dos adesivos E&R. No entanto, os novos adesivos, os Self-etch, não necessitam deste condicionamento total, pois na sua composição já apresentam componentes que realizam esse passo. Cada ingrediente tem até certo ponto, um efeito específico sobre a resistência de união, a eficiência de ligação, a durabilidade de união, vida útil e a biocompatibilidade do adesivo. No entanto, os ingredientes que constituem estes adesivos podem afetar-se entre si e provocarem interações complexas. Ao todo, a composição química que constituem os adesivos autocondicionantes determina o seu sucesso ou não. Daí que o conhecimento da composição, das características e dos mecanismos de adesão de cada sistema adesivo é fundamentalmente importante para permitir a adoção de estratégias de ligação ideais nas várias condições clínicas apresentadas. Posto isto, resolveu-se realizar esta revisão bibliográfica para tentar perceber a complexidade destes adesivos, suas vantagens e limitações, pois como estes adesivos apresentam misturas bastante complexas, o profundo conhecimento destes ingredientes é a chave para uma melhor compreensão do comportamento dos adesivos nos estudos e na clínica. All adhesives consist of products designed to perform the connection between certain restorative materials and dental tissues to the union. The self-etching adhesives were recently introduced and present a strategy based on the adhesive action of the acidic monomers that simultaneously condition the dental substrates. The total acidic conditioning is the basis of contemporary adhesives, namely, adhesives Etch-and-rinse. However, new adhesives, Self-etch, do not require this full capacity because they already have in their composition components that perform this step. Each ingredient has to some extent a specific effect on the bond strength, the coupling efficiency, the durability of union, lifetime and the biocompatibility of the adhesive. However, the ingredients of these adhesives can affect each other and cause complex interactions. Altogether, the chemical composition constituting the self-etching adhesives determines your success or not. Hence the knowledge of the composition, characteristics and mechanisms of adhesion of each adhesive system is fundamentally important to enable the adoption of strategies for optimal bonding in various clinical conditions presented. That said, we decided to conduct this literature review to try to understand the complexity of these adhesives, its advantages and limitations, because as these adhesives have very complex mixtures, deep knowledge of these ingredients is the key to a better understanding of the behavior of adhesives in studies and clinical.

Orientador: Milton Carlos Kuga
Resumo: O objetivo dos estudos são avaliar a capacidade de limpeza superfie dentinaria impregnada por AH Plus e MTA Fillapex, proporcionada pelo etanol a 95,0% (E) ou xilol (X) e seus efeitos sobre a interface adesiva e resistência de união do sistema adesivo etch-and-rinse, com condicionamento ácido (CA) imediato (I) ou após 7 dias (T). Publicação 1: Cinquenta espécimes de coroas de incisivos bovinos foram impregnados com o cimento e divididos em quatro grupos (n=10): G1(EICA), E e CA imediato; G2(XICA), X e CA imediato; G3(ETCA), E e CA após 7 dias e G4(XTCA), X e CA após 7 dias e G5(controle), CA imediato. Escores foram atribuídos, em relação à persistência de resíduos na dentina, por análises em MEV(500X). Cinquenta fragmentos foram preparados, restaurados com resina composta e obtidas imagens em microscopia confocal laser (1024X), para avaliar a formação de camada hibrida, mensurada no Image J. Cinquenta fragmentos foram igualmente preparados e submetidos ao teste de microcisalhamento para avaliar os efeitos sobre a resistência de união do sistema adesivo etch-and-rinse na dentina. Em relação à persistência de resíduos, G1 e G2 apresentaram maiores valores que G3 e G4 (P<0,05). Entre G1 e G2 ou G3 e G4 não houve diferença (P>0,05). Em relação à interface adesiva, a extensão da formação da camada hibrida foi G5>G4=G3=G2=G1. Em relação à resistência de união do sistema adesivo G5=G4 e G4=G2 (P=0,05), porém G5>G2 (P<0,05) e G1=G2=G3 (P>0,05). Publicação 2: Cinquenta espécimes de co... (Resumo completo, clicar acesso eletrônico abaixo)
Abstract: The aim was to evaluate the cleaning protocol in dentin impregnated with different endodontic sealers using 95% ethanol (E) or xylol (X) and its effects on adhesive interface and on bond strength of etch-and-rinse adhesive system when the acid etching (AE) was immediately (I) carried out or 7 days delay (D).Publication 1:Fifty bovine incisors specimens were impregnated with epoxy resin-based sealer (AH Plus) sealer and divided into four groups (n = 10): G1 (EIAE); G2 (XIAE); G3 (EDAE); G4 (XDAE) and G5 (control, IAE). The persistence of residues was evaluated using scores by SEM (500X). Fifty fragments were prepared similarly as described before, restored with composite resin and subjected to laser confocal microscopy (1024X). The hybrid layer formation was measured using Image J program. Another fifty fragments were similarly prepared and submitted to microshear bond test to access the bond strength of etch-and-rinse adhesive system to dentin.Regarding the persistence of residues, G1 and G2 presented higher values than G3 and G4 (P<0.05). No statistical difference was found between G1 and G2 or G3 and G4 (P>0.05). Regarding the adhesive interface, the extend of hybrid layer formation G5>G4=G3=G2=G1.Regarding the bond strength of adhesive system: G5=G4 and G4=G2 (P=0.05), however G5>G2 (P<0.05) and G1=G2=G3 (P>0.05).Publication 2: Fifty bovine crown specimens were impregnated with mineral trioxide aggregate-based (MTA) sealer and divided into four groups (n = 10): G1 (EIAE); G2 (XIAE); G3 (EDAE); G4 (XDAE) and G5 (control, IAE). The residues persistence using scores by SEM (500x). Fifty fragments were prepared similarly as described before and subjected to laser confocal microscopy (1024X). The hybrid layer formation was measured using Image J program. Fifty fragments were similarly prepared and submitted to microshear bond test to access the bond strength of etch-and-rinse ...(Complete abstract electronic access below)
Doutor

Made available in DSpace on 2014-06-11T19:24:07Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-07-05Bitstream added on 2014-06-13T19:51:19Z : No. of bitstreams: 1 silva_prp_me_sjc.pdf: 750069 bytes, checksum: 94263aef7c378118e8087ea9d933ad86 (MD5)
Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
O objetivo desta pesquisa foi avaliar a influência do laser Nd:YAG nas propriedades mecânicas (dureza e módulo de elasticidade) da interface adesiva, utilizando a técnica da nanoindentação, empregando-se sistema adesivo convencional Adper Single Bond 2 – 3M ESPE (SB) ou autocondicionante Clearfil SE Bond – Kuraray (CSE). Doze terceiros molares humanos tiveram suas superfícies oclusais desgastadas até a exposição da dentina superficial. Uma cavidade circular padronizada com fresa 3053 foi realizada na superfície oclusal proporcionando 2 mm de dentina remanescente. Os espécimes foram embutidos em resina acrílica, e seccionados no sentido mésio-distal, sendo as 24 hemi-coroas obtidas divididas em quatro grupos: Grupo controle (SBC) - aplicação do sistema SB de acordo com as recomendações do fabricante; Grupo laser (SBL) - aplicação do sistema adesivo SB e tratamento com laser Nd:YAG (140mJ/cm2/60s/não contato); Grupo controle (CSEC) - aplicação do sistema adesivo autocondicionante CSE de acordo com as recomendações do fabricante; Grupo laser (CSEL)- aplicação do sistema adesivo autocondicionante CSE e tratamento com laser Nd:YAG (140mJ/cm2/60s/não contato). Após a polimerização dos sistemas adesivos, foram aplicados dois incrementos da resina composta Filtek Z 350 (3M ESPE). Os corpos-de-prova foram imersos em água destilada e armazenados por 24h em estufa 37ºC e submetidos à nanoidentação em aparelho Nano Indenter® XP (MTS®, MN, EUA).. Os resultados foram submetidos aos testes estatísticos de Análise de Variância (ANOVA), Tukey e t-Student (p<0,05). Concluiu-se que a aplicação do laser Nd:YAG em ambos os sistemas adesivos não alterou o nível de dureza da interface adesiva, no entanto alterou o módulo de elasticidade
The aim of this study was to evaluate the influence of Nd: YAG laser on the mechanical properties (hardness and modulus of elasticity) of the adhesive interface, using the technique of nanoindentation, employing conventional adhesive system Single Bond 2 3M ESPE (SB) or selfetching adhesive system Clearfil SE Bond - Kuraray (CSE). On 12 human molars, a flat superficial dentin surface was exposed by abrasion. A standardized circular cavity with bur 3053 was performed on the occlusal surface and dentin thickness was standardized in 2 mm. The specimens were embedded in resin acrylic and sectioned mesio-distally through their long axes, and the 24 hemi-crowns obtained divided into four groups: Control Group (SBC) – the application of SB system according to the manufacturer's recommendations; Laser Group (SBL) – SB adhesive system and treatment with Nd: YAG laser (140mJ/cm2/60s/no contact) Control Group (CSEC) – application of CSE self-etching adhesive system according to the manufacturer's recommendations; Laser Group (CSEL) – application of CSE self-etching adhesive system and treatment with Nd: YAG laser (140mJ/cm2/60s/no contact). After polymerization of the adhesives, were applied two increments of composite resin Filtek Supreme and specimens were immersed in distilled water and stored for 24 hours at 37 ºC and submitted to nanoidentation in Nano Indenter ® XP (MTS ®, MN, USA. Nanoindentation were made on composite resin, adhesive system, hybrid layer and dentin. The results were analyzed by a tree-way ANOVA, Tukey and e t-Students (p<0,05). It was concluded that the application of Nd:YAG laser in both adhesive systems did not change hardness level of hybrid layer, however chanded the elastic modulus

Orientador: Sérgio Eduardo de Paiva Gonçalves
Banca: Alessandra Bühler Borges
Banca: Andrea Anido Anido
Resumo: O objetivo desta pesquisa foi avaliar a influência do laser Nd:YAG nas propriedades mecânicas (dureza e módulo de elasticidade) da interface adesiva, utilizando a técnica da nanoindentação, empregando-se sistema adesivo convencional Adper Single Bond 2 - 3M ESPE (SB) ou autocondicionante Clearfil SE Bond - Kuraray (CSE). Doze terceiros molares humanos tiveram suas superfícies oclusais desgastadas até a exposição da dentina superficial. Uma cavidade circular padronizada com fresa 3053 foi realizada na superfície oclusal proporcionando 2 mm de dentina remanescente. Os espécimes foram embutidos em resina acrílica, e seccionados no sentido mésio-distal, sendo as 24 hemi-coroas obtidas divididas em quatro grupos: Grupo controle (SBC) - aplicação do sistema SB de acordo com as recomendações do fabricante; Grupo laser (SBL) - aplicação do sistema adesivo SB e tratamento com laser Nd:YAG (140mJ/cm2/60s/não contato); Grupo controle (CSEC) - aplicação do sistema adesivo autocondicionante CSE de acordo com as recomendações do fabricante; Grupo laser (CSEL)- aplicação do sistema adesivo autocondicionante CSE e tratamento com laser Nd:YAG (140mJ/cm2/60s/não contato). Após a polimerização dos sistemas adesivos, foram aplicados dois incrementos da resina composta Filtek Z 350 (3M ESPE). Os corpos-de-prova foram imersos em água destilada e armazenados por 24h em estufa 37ºC e submetidos à nanoidentação em aparelho Nano Indenter® XP (MTS®, MN, EUA).. Os resultados foram submetidos aos testes estatísticos de Análise de Variância (ANOVA), Tukey e t-Student (p<0,05). Concluiu-se que a aplicação do laser Nd:YAG em ambos os sistemas adesivos não alterou o nível de dureza da interface adesiva, no entanto alterou o módulo de elasticidade
Abstract: The aim of this study was to evaluate the influence of Nd: YAG laser on the mechanical properties (hardness and modulus of elasticity) of the adhesive interface, using the technique of nanoindentation, employing conventional adhesive system Single Bond 2 3M ESPE (SB) or selfetching adhesive system Clearfil SE Bond - Kuraray (CSE). On 12 human molars, a flat superficial dentin surface was exposed by abrasion. A standardized circular cavity with bur 3053 was performed on the occlusal surface and dentin thickness was standardized in 2 mm. The specimens were embedded in resin acrylic and sectioned mesio-distally through their long axes, and the 24 hemi-crowns obtained divided into four groups: Control Group (SBC) - the application of SB system according to the manufacturer's recommendations; Laser Group (SBL) - SB adhesive system and treatment with Nd: YAG laser (140mJ/cm2/60s/no contact) Control Group (CSEC) - application of CSE self-etching adhesive system according to the manufacturer's recommendations; Laser Group (CSEL) - application of CSE self-etching adhesive system and treatment with Nd: YAG laser (140mJ/cm2/60s/no contact). After polymerization of the adhesives, were applied two increments of composite resin Filtek Supreme and specimens were immersed in distilled water and stored for 24 hours at 37 ºC and submitted to nanoidentation in Nano Indenter ® XP (MTS ®, MN, USA. Nanoindentation were made on composite resin, adhesive system, hybrid layer and dentin. The results were analyzed by a tree-way ANOVA, Tukey and e t-Students (p<0,05). It was concluded that the application of Nd:YAG laser in both adhesive systems did not change hardness level of hybrid layer, however chanded the elastic modulus
Mestre

The Idea of using root canals as retention places in endodontically treated teeth is not new. The postLs function is to provide retention and support to restorative materials. Adhesive cementation of glass fiber posts and the consequent core build up of a weakened tooth is a critical procedure, because of the several concerns involved and the great amount of materials available on the market and its different protocol instructions. This study evaluated the influence of different post configurations, post surface treatments and adhesive systems on retention of glass fiber posts on artificial root canals made of composite resin. The dual cure adhesive Excite DSC Soft Touch EndoR and the chemically activated adhesive LOKR were tested. Silane coupling agent and sandblasting with alumina oxide at 50Êm were the different surface treatments tested. The different post configurations were serrated posts or smooth posts. After cementation, the specimen were stored in distilled water at 37C for 5 days and then su bmitted to push-out tests. Also the type of failure was recorded. The adhesive Excite DSC Soft Touch EndoR was the most retentive. And, after microscopical observation it was concluded that sandblasting and serrated posts exhibited better performance than silane coupling agent on retention of the posts.
A idéia de se usar os condutos radiculares como pontos de retenção em dentes tratados endodonticamente nao e nova. A funcao do pino e de prover retencao e suporte para os materiais restauradores. A cimentacao adesiva de pinos de fibras de vidro e a consequente reconstrucao do dente debilitado sao procedimentos criticos, tanto pelas variaveis envolvidas como pela enorme gama de materiais disponiveis no mercado e seus diversos protocolos de utilizacao. O presente trabalho avaliou a influencia de diferentes configuracoes superficiais, tratamentos de superficie e sistemas adesivos na retencao de pinos de fibras de vidro em canais artificiais de resina composta. O adesivo de presa dual ExciteR DSC Soft Touch Endo e o adesivo quimicamente ativado LOKR foram testados. Os tratamentos dados aos pinos foram: silanizacao e jateamento com oxido de aluminio de 50Êm, e as configuracoes de superficie foram os pinos lisos ou serrilhados. Os especimes, apos cimentacao em canais artificiais de resina composta e armazenados em agua destilada a 37C durante 5 dias, foram submetidos a testes de tracao para medicao da forca de tracao. Alem disso, ainda foram feitas observacoes em microscopio optico com aumento de 15x para se determinar os tipos de falha (adesiva na interface pino/cimento; adesiva na interface canal/cimento ou coesiva da resina do canal). Foi encontrado que o adesivo ExciteR DSC Soft Touch Endo foi superior na resistencia adesiva. E que sob observacao em microscopio optico, pode-se perceber uma melhor performance do jateamento e da superficie serrilhada sobre a silanizacao.

The aim of this study was to evaluate the effect of dentin pretreatment with chlorhexidine and sodium hypochlorite in the bond strength of adhesive systems. Seventy-two sound human third molars were divided in 12 groups according to the adhesive system (Single Bond 2 - SB2, Clearfil SE Bond - SE, Single Bond Universal - SBU ) pretreatment (control, 2% chlorhexidine and hypochlorite sodium 10% ) and strategies ( self-etching or total etching ). The adhesive protocols followed the recommendation of the respective manufacturers and resin restorations were made of 5mm. After restoration, the teeth were stored in distilled water for 24 hours and sectioned to obtain specimens with interface area of 1.0 mm². Then, the specimens were subjected to microtensile testing in a universal testing machine until its failure. The results of the test microtensile bond strength were recorded in Mpa. Mean and standard deviation were calculated for each of the experimental groups. The mean bond strengths were subjected to analysis of variance (ANOVA) and differences between groups were assessed by Tukey test. For all analyzes the significance level was 5%. Analysis of variance showed that treatment surface factor exerted significant influence on the values of bond strength. The use of sodium hypochlorite to 10 % reduced the values of bond strength when compared to other treatments for all adhesive systems and should not be considered as a pretreatment of dentin.
O objetivo deste estudo foi avaliar o efeito de pré-tratamentos dentinários com clorexedina e hipoclorito de sódio, na resistência de união de sistemas adesivos. Setenta e dois terceiros molares humanos hígidos foram alocados em quatro grupos experimentais de acordo com o sistema adesivo (Single Bond 2 SB2, Clearfil SE Bond SE, Single Bond Universal - SBU) pré-tratamento (controle, Clorexedina 2% e Hipoclorito de Sódio 10%) e estratégias de uso (autocondicionante ou condicionamento ácido total). Os protocolos adesivos seguiram recomendação dos respectivos fabricantes e restaurações de resina de 5mm foram confeccionadas. Após restaurados, os dentes foram armazenados em água destilada durante 24h e seccionados para obtenção dos espécimes com área na interface de 1,0 mm² . Em seguida, os espécimes foram submetidos ao ensaio de microtração em máquina de ensaios universais até a ruptura. Os resultados de resistência adesiva ao ensaio de microtração foram registrados em MPa e elaboradas médias e desvios padrão para cada um dos grupos experimentais. As médias de resistência adesiva foram submetidas à análise de variância (ANOVA) e as diferenças entre os grupos foram submetidas ao teste de Tukey. Para todas as análises, o nível de significância considerado foi de 5%. A análise de variância mostrou que o fator tratamento de superfície exerceu influência significante nos valores de resistência de união. A aplicação de hipoclorito de Sódio a 10% reduziu os valores de resistência de união quando comparados aos tratamentos controle e clorexedina para todos os sistemas adesivos testados, não devendo portanto ser considerado como um pré-tratamento em dentina.

Monografia apresentada à Universidade Fernando Pessoa para obtenção do grau Licenciada em Medicina Dentária
Este estudo de revisão bibliográfica foca um tema que surge com muita frequência na prática clínica diária do médico dentista: os adesivos dentários. A escolha do melhor sistema adesivo permanece ainda incerta e este trabalho visa a avaliação dos diferentes desempenhos clínicos dos sistemas actuais, ou seja, os adesivos de condicionamento total e os de auto condicionamento. The aim of this systematic review is the dental adhesives. The pertinence of this subject increases if we consider their implications in the dentist`s clinical practice. Choosing the better adhesive system still remains uncertain and this survey evaluates the different clinical performances of the actual systems, total-etch and self-etch adhesives.

Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde. Programa de Pós-Graduação em Odontologia.
Made available in DSpace on 2012-10-24T09:54:18Z (GMT). No. of bitstreams: 1 265559.pdf: 9972981 bytes, checksum: 21d2a7f51e034815708f9f2861c652d5 (MD5)
Este estudo in vitro foi realizado com o objetivo de avaliar a resistência à microtração, e a nanoinfiltração de sistemas adesivos em dentina decídua, imediatamente (IM) e após seis meses (6M) do procedimento adesivo. Coroas de molares decíduos, hígidos e extraídos, foram desgastadas com papel de carbeto de silício até a granulação 600, obtendo-se superfícies oclusais planas, distribuídas em quatro grupos: Scotchbond Multi-Purpose (SMP), Single Bond (SB), Clearfil SE Bond (CSB) e Adper Prompt L-Pop (APL). Baseado nos dados obtidos pôde-se concluir que a resistência adesiva e a nanoinfiltração não foram influenciadas pelo envelhecimento e que a expressão da nanoinfiltração foi diferente entre os adesivos de condicionamento ácido total e autocondicionantes.

Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2015.
Made available in DSpace on 2016-10-19T13:18:54Z (GMT). No. of bitstreams: 1 338968.pdf: 26388567 bytes, checksum: 2069b93e85f123b8ac3c78a879aef322 (MD5) Previous issue date: 2015
Objetivos: Avaliar o efeito de diferentes tratamentos de superfície e do tempo de armazenamento na resistência de união adesiva à microtração (µTBS) de blocos CAD/CAM do tipo resina-cerâmica. Materiais e Métodos: Dois tipos de blocos CAD/CAM resina-cerâmica (Cerasmart, GC e Enamic, Vita Zahnfabrik) foram seccionados em fatias com 4 mm de espessura, distribuídos em seis grupos e submetidos aos seguintes tratamentos de superfície: Grupo 1: sem tratamento; Grupo 2: jateamento com óxido de alumínio 27 µm + silano; Grupo 3: condicionamento com ácido hidrofluorídrico 5% por 60 seg + silano; Grupo4: condicionamento com ácido fosfórico 37% por 60 seg + silano; Grupo 5: jateamento; Grupo 6: jateamento + silano. Pares de fatias do mesmo material e grupo foram cimentadas umas às outras (n=3 espécimes sanduíches/grupo) utilizando um cimento resinoso dual autoadesivo para os grupos 1 ao 5, e uma resina fluida fotopolimerizável para o grupo 6. Após respectivamente três semanas e 6 meses de armazenamento em cloramina 0,5% à 37oC, os espécimes sanduíches foram seccionados em micro espécimes retangulares, desgastados na interface adesiva (forma de ampulheta) e submetidos ao teste de µTBS. Os dados foram estatisticamente analisados por um modelo linear de efeitos mistos considerando como fatores o tipo de material, o tratamento de superfície e o tempo de armazenamento, assim como suas interações de primeiro grau(p=0,05). Resultados: Independente do tratamento de superfície e tempo de armazenamento, os dois materiais resina-cerâmica apresentaram valores deµTBS sem diferença estatística. Após 3 semanas, todos os grupos obtiveram valores similares. Depois de 6 meses, os valores de resistência adesiva foram mantidos quando foi realizado o JAT com óxido de alumínio (Grupo 263) ou o condicionamento com HF (Grupo 5), ambos seguidos por silanização. O JAT seguido de silanização e o uso de uma resina fluida como agente cimentante também manteve a µTBS. A ausência de tratamento superficial (Grupo 1), o JAT isolado (Grupo 2) e o condicionamento com H3PO4 seguido de silanização (Grupo 6) resultaram em uma diminuição da µTBS. Conclusões: ambos materiais do tipo resina-cerâmica demonstraram µTBS similar, independente do tratamento de superfície. A criação de uma superfície microrretentiva através do JAT com óxido de alumínio ou condicionamento com HF, seguido de silanização, é necessária para manutenção resistência de união adesiva após 6 meses.

Objectives: To evaluate the effect of different surface treatments on the bond strength to resin-ceramic CAD/CAM blocks after six months. Materials and Methods: Two types of resin-ceramic CAD/CAM blocks (Cerasmart, GC; Enamic, Vita Zahnfabrik) were cut in slabs of 4-mm thickness, divided into six groups and subjected to the following surface treatments: Group 1: No treatment; Group 2: Sandblasting (SB); Group 3: SB + Silane; Group 4: SB + Silane; Group 5: 5% Hydrofluoric acid (HF) etching + Silane; Group 6: 37% Phosphoric acid (H3PO4) etching + Silane. Sections of the same group were luted together (n=3 sandwich specimens/group) using a dual-cure self-adhesive cement for all groups, except for Group 4 that were luted using a flowable light-curing composite. After three weeks of storage in 0.5% chloramine at 37oC, the sandwich specimens were sectioned in rectangular micro-specimens and trimmed to an hourglass shape. Part of the specimens was subjected to a micro-tensile bond strength (µTBS) test and the other half was tested after 6 months of storage. Data were statistically analyzed with a linear mixed effects model for the factors surface treatment, material type and storage period, together with their first-degree interactions (p=0.05). Results: The lowest bond strengths were obtained in the absence of any surface treatment (Group 1), while the highest bond strengths were obtained when the surface was roughened by either SB or HF etching, this in combination with chemical adhesion through silanization. Loss in bond strength was observed after six months when either surface roughening or silanization, or both, were omitted. Conclusions: Both resin-ceramic CAD/CAM blocks appeared equally bonding-receptive regardless of the surface treatment. Creating a microretentive surface by either SB or HF etching, followed by chemical adhesion using a silane coupling agent is mandatory to maintain the bond strength after six months.

Novos métodos de remoção do tecido cariado tem sido propostos, entre eles a utilização de lasers, abrasão a ar e químico-mecânico. Este trabalho teve o objetivo de avaliar a influência de diferentes métodos de remoção de cárie na resistência de união de um sistema adesivo autocondicionante. Cinquenta molares humanos cariados extraídos foram desgastados para expor uma superfície plana onde a lesão de cárie se encontrava rodeada por dentina hígida. Os dentes foram divididos em 05 grupos (n=10), com um total de 50 dados, de acordo com o método de remoção do tecido cariado, como segue: G1 - sem remoção; G2 - remoção com lixa; G3 – broca de aço esférica em baixa rotação; G4 - laser de Er, Cr: YSGG e G5 - Carisolv. Procedimentos adesivos foram realizados com o sistema autocondicionante (Clearfil SE Bond – Kuraray – Japão), de acordo com as instruções do fabricante. Um cilíndro de resina composta (Z250- 3M do Brasil) foi construído sobre a superfície com o sistema adesivo e estocados em água (24 horas a 37 0 C). Os corpos de prova foram seccionados verticalmente para obtenção de fatias e em seguida confeccionadas ampulhetas em dentina infectada, afetada e sadia, com área aproximada de 1mm 2. As ampulhetas foram montadas em dispositivos de micro-tração e ensaiados na máquina de teste (Mini-Instron) com velocidade de 0,5mm/min. Os resultados obtidos mostraram que existem diferenças estatisticamente significantes entre os substratos sadio e infectado para o grupo G1e sadio e afetado para os grupos G2, G3 e G5. Em dentina sadia, o método utilizado em G3 resultou em valores de adesão superiores com relação a G4 e G2 foi estatisticamente superior com relação a todos os grupos. Os métodos de remoção de dentina infectada utilizados em G2 e G3 resultaram em valores de adesão superiores com relação a G1(dentina infectada). Desta forma podemos concluir que: o tipo de substrato influencia significativamente na resistência adesiva do sistema autocondicionante testado. A adesão à dentina sadia é mais efetiva que à dentina infectada (G1) e à dentina afetada obtida após remoção do tecido infectado com lixa (G2), broca (G3) e Carisolv (G5). Entretanto, para o laser de Er,Cr:YSGG (G4) não houve evidência amostral que sugerisse maior efetividade na adesão da dentina sadia com relação à dentina afetada. A adesão em dentina sadia mostrou-se mais efetiva quando esta foi instrumentada com lixa. Porém, trata-se de um recurso laboratorial de padronização dos espécimes. A utilização da broca de aço resultou em uma superfície mais favorável a adesão, quando comparada à obtida após irradiação com laser de Er, Cr: YSGG, em dentina sadia. A adesão em dentina infectada é pobre, ficando ressaltada a necessidade da remoção deste tipo de dentina, preferencialmente com lixa ou broca, previamente a adesão com sistema autocondicionante. Para os demais métodos de remoção da dentina infectada testados, não houve evidência amostral para se detectar a existência de diferenças significantes na resistência adesiva em dentina afetada.
New methods for carious dentine removal have been proposed, such as, lasers and chemo-mechanical. This in vitro study aimed to evaluate the influence of caries removal methods (steel burs, Er, Cr: YSGG laser and Carisolv) on microtensile bond strength of self-etching adhesive systems. 50 extracted carious human molars were ground to expose flat surfaces where caries lesion was surrounded by normal dentine. Teeth were divided into 5 groups (n=10), with 50 original data, according to the removal method used: G1 - no removal; G2 - abrasive paper, G3 - steel burs; G4 – Er, Cr: YSGG laser (79, 61 J/cm 2 ) and G5 – Carisolv. Surfaces were bonded with Clearfil SE Bond, according to manufacturers’ instructions. A crown was built up using composite resin (Z250- 3M Brasil). After storage in water (24 h, 37 0 C), teeth were vertically serially sectioned into slices and trimmed into an hourglass shape with about of 1mm 2 area at the adhesion interface, that contained either infected, caries affected and normal dentine. Samples were tested in tension in a Instron machine at 0,5mm/min. Results showed that there is a significant difference between tested groups (p< 0.005). Significantly lower results were found for caries infected dentin when compared to normal dentin values (G1). A significant difference was also found when caries affected and normal dentin were compared (G2, G3, G5). In normal dentin, G2 showed better bond strenght than another groups and G4 showed lower results than G3. G2 and G3 caries infected dentin removal methods showed better bond strength than the other groups when compared with G1 (caries infected dentin). The results indicated that: bond strength of a self-etching system to normal dentin was better than to caries infected (G1) and caries affected dentin after the use of abrasive paper (G2), round steel bur (G3) and Carisolv (G4). However, there was no difference between caries affected and normal dentin after the use of ErCr:YSGG laser (G4); abrasive paper is a laboratorial method to create smear layer and it was responsable for the best bond strength to normal dentin. The usage of Er, Cr: YSGG laser negatively altered adhesion of self-etching system on normal dentin when compared with round steel bur; infected dentin is not an adequate substrate for adhesion. Abrasive paper and round steel bur are the best caries infected dentin removal methods. There were no difference in bond strength to caries affected dentin when the other methods were used.